Dechlorination of MCAA with Zero-valent Iron supported by PVDF-TiO 2 Film

Zhi Xia,Huiling Liu,Shan Wang,Zhaohong Meng

2012-01-01

Abstract:In order to improve the dechlorination efficiency of monochloroacetic acid (MCAA) by flim-supported zero-valent iron (ZVI), Poly(vinylidene fluoride) (PVDF) modified by adding titanium dioxide (TiO 2) nanoparticles was prepared by phase inversion method as the support of ZVI. The modified PVDF films were characterized by measurement of contact angle, BET analysis and Fourier transform infrared spectroscopy (FT-IR). TiO 2 adding content was optimized through iron loading experiments and dechlorination of MCAA. The results show that the optimal TiO 2 adding content is 1.0wt%; when TiO 2 adding content is below 1.0wt%, the more TiO 2 nanoparticles are added, the more hydrophilicity and specific surface area of support film are showed; when TiO 2 adding content is above 1.0wt%, hydrophilicity and specific surface area of support film decrease with increase of TiO 2 adding content because of assembling of TiO 2 nanoparticles. The Dechlorination efficiency of MCAA with ZVI supported by PVDF-TiO 2 film in 30 min reached 34.73%, which raised 23.53% more than with ZVI supported by unmodified PVDF film.