Abstract:We report on the cooperative energy transfer process in RE3+-Yb3+ (RE=Pr, Tm and Tb) codoped transparent glass-ceramics containing CaF2 nanocrystals, which are capable of splitting a visible photon absorbed by RE3+ into two near infrared photons emitted by Yb3+. The formation of CaF2 nanocrystals in the glass-ceramics was confirmed by X-ray diffraction measurement. Yb3+ emission in the wavelength range of 950- 1100 nm (F-2(5/2) -> F-2(7/2)) was observed upon the excitation of P-3(0) energy level of Pr3+ at 482 nm, (1)G(4) energy level of Tm3+ at 468 nm, and D-5(4) energy level of Tb3+ at 484 nm, respectively, in the RE3+-Yb3+ co-doped glass-ceramics. The energy transfer process was proved by the excitation and emission spectra. The Yb3+ concentration dependent quantum efficiency was also evaluated individually in the codoped systems, which indicated that Pr3+-Yb3+ is the most efficient cooperative energy transfer couple. It was supposed that besides the cooperative energy transfer process, the (1)G(4) state, which may be populated by P-3(0)->(1)G(4) transition as a result of energy transfer to one Yb3+ ion from Pr3+ P-3(0) energy level, can also act as a donor state in the energy transfer to another Yb3+ ion. These rare-earth ions codoped transparent glassy materials may have potential applications for the enhancement of photovoltaic conversion efficiency of silicon solar cells via spectra modification.

A discussion on spectral modification from visible to near-infrared based on energy transfer for silicon solar cells

Broadband downshifting luminescence of Cr 3+/Yb 3+-codoped fluorosilicate glass

Near-infrared Emission of Yb3+ Through Energy Transfer from ZnO to Yb3+ in Glass Ceramic Containing ZnO Nanocrystals.

Ultraviolet to Near-Infrared Spectral Modification in Ce3+ and Yb3+ Codoped Phosphate Glasses

Energy Transfer Between Silicon–oxygen-Related Defects and Yb3+ in Transparent Glass Ceramics Containing Ba2TiSi2O8 Nanocrystals

Sensitized Yb3+ Luminescence of Eu3+/Yb3+‐Codoped Fluorosilicate Glass Ceramics

Near-Infrared Down-Conversion In Rare-Earth-Doped Chloro-Sulfide Glass Ges2-Ga2s3-Cscl: Er, Yb

Near-infrared quantum cutting and energy transfer mechanism in Lu 2 O 3 : Tm 3+ /Yb 3+ phosphor for high-efficiency photovoltaics

Conversion Of Near-Ultraviolet Radiation Into Visible And Infrared Emissions Through Energy Transfer In Yb2o3 Doped Sro-Tio2-Sio2 Glasses

Energy Transfer and Frequency Upconversion in Er3+-Yb3+ Codoped Oxy-Fluoro-tungstosilicate Glasses

Cooperative Downconversion Luminescence in Pr 3+ /yb 3+ :Sio 2 –al 2 O 3 –baf 2 –gdf 3 Glasses

Near-infrared quantum cutting and energy transfer mechanism in Lu2O3: Tm3+/Yb3+ phosphor for high-efficiency photovoltaics

Spectral Modification And Quantum Cutting In Re3+-Yb3+ (R=Pr, Tm, And Tb) Codoped Transparent Glass-Ceramics Containing Caf2 Nanocrystals

Broadband Spectral Modification from Visible Light to Near-Infrared Radiation Using Ce3+-Er3+ Codoped Yttrium Aluminium Garnet

Effect of Zn/Si ratio on conversion luminescent properties of Er3+/Yb3+ co-doped oxyfluoride glasses used for solar cells

Near-Infrared Emission From Eu-Yb Doped Silicate Glasses Subjected To Thermal Reduction

Spectroscopic Properties Of Er3+/Yb3+ Co-Doped 50sio(2)-20al(2)O(3)-30caf(2) Glass And Glass Ceramics

Broadband Spectral Conversion of Visible Light to Near-Infrared Emission Via Energy Transfer from Ce3+ to Nd3+/Yb3+ in YAG

Broadband sensitized near‐infrared emission in Eu2+‐Nd3+ co‐doped BaAl2O4 as a potential spectral modulator for silicon solar cells

Spectroscopic Properties Of Er3+ And Yb3+ Co-Doped Glass Ceramics Containing Srf2 Nanocrystals

Effect of ZnO on structure and luminescence properties of Ce3+-Yb3+ co-doped Na2O–CaO–SiO2–Al2O3 glasses for solar panel applications