Abstract:LiNi0.5Mn1.5O4 (LNMO) is a promising high-performance lithium-ion battery cathode material. We synthesized various structures of LNMO precursors based on two calculations, using the solution combustion method with different fuel ratios. The precursors were annealed for a short time under ambient atmospheric conditions, and various polyhedral structures of LNMO samples were formed through natural oxygen absorption. The results reveal that lower fuel ratios (0.2) cause the samples having incomplete crystal structures and severe particle aggregation, resulting in higher polarization and poorer electrochemical performance. Samples with higher fuel ratios (0.8) exhibit complete crystal structures, lower polarization, and excellent rate performance. At 20 C, the electrochemical capacity of sample with fuel ratios (0.8) can reach 90.47 mAh/g. Samples with theoretical fuel ratios (0.5) show the best electrochemical cycling performance, capacity retention, and cycling stability. After 200 cycles at 1 C, the electrochemical capacity still maintains 123.08 mAh/g, with a capacity retention rate of 96.5%. The results indicate that the formation of the precursor, oxygen absorption during annealing, polyhedral structures, different redox couples, and stability of the electrode/electrolyte interface have significant effects on the electrochemical performance. In , our research provides insights into the solution combustion synthesis of high-performance LNMO cathode materials, emphasizing the importance of accurate calculation of synthesis parameters to achieve optimal electrochemical performance.

A Novel Solution Combustion Synthesis of Cobalt Oxide Nanoparticles As Negative-Electrode Materials for Lithium Ion Batteries

Scalable Synthesis of Fe3O4/C Composites with Enhanced Electrochemical Performance As Anode Materials for Lithium-Ion Batteries

Eruption Combustion Synthesis of NiO/Ni Nanocomposites with Enhanced Properties for Dye-Absorption and Lithium Storage.

Solution combustion synthesis of a nanometer-scale Co 3 O 4 anode material for Li-ion batteries

Solution-combustion Synthesis of Nanomaterials for Lithium Storage

Solution Combustion Synthesis of Submicron-Sized Titanium Niobium Oxide Anodes for High-Rate and Ultrastable Lithium-Ion Batteries.

Solution Combustion Synthesis of Mesoporous Mesh-Structured Co3O4/C Composites As Anode Materials for Lithium Storage

Combustion Synthesis and Electrochemical Performance of Li [li0.2mn0.54ni0.13co0.13]o2 with Improved Rate Capability

Solution Combustion Synthesis of High-Performance Nano-LiFePO4/C Cathode Material from Cost-Effective Mixed Fuels

Combustion Synthesized Rod-Like Nanostructure Hematite with Enhanced Lithium Storage Properties

Synthesis of nanoscale CoO particles and their effect on the positive electrodes of nickel–metal hydride batteries

Novel and highly efficient catalyst for Li–O2 battery: Porous LaCo0.6Ni0.4O3 nanofibers decorated with ultrafine Co3O4 nanoparticles

Nano-sized Cobalt Oxide/mesoporous Carbon Sphere Composites As Negative Electrode Material for Lithium-Ion Batteries

High-Loading Nickel Cobaltate Nanoparticles Anchored on Three-Dimensional N-Doped Graphene as an Efficient Bifunctional Catalyst for Lithium-Oxygen Batteries

Well-Dispersed Co/CoO/C Nanospheres with Tunable Morphology as High-Performance Anodes for Lithium Ion Batteries

Optimizing Solution Combustion Method Fuel Ratios for Enhanced Electrochemical Performance of LiNi0.5Mn1.5O4 Cathode Materials

In-situ exsolution of CoNi alloy nanoparticles on LiFe<sub>0.8</sub>Co<sub>0.1</sub>Ni<sub>0.1</sub>O<sub>2</sub> parent: New opportunity for boosting oxygen evolution and reduction reaction

From Cobalt Nitrate Carbonate Hydroxide Hydrate Nanowires To Porous Co3o4 Nanorods For High Performance Lithium-Ion Battery Electrodes

Enhancing Electrode Performance by Exsolved Nanoparticles: A Superior Cobalt-Free Perovskite Electrocatalyst for Solid Oxide Fuel Cells.

Synthesis of Iron Oxide-Ton Oxide-Carbon Composite Nanobelts and Their Applications in Lithium-Ion Batteries

A cobalt-free Li(Li0.17Ni0.17Fe0.17Mn0.49)O2 cathode with more oxygen involving charge compensation for lithium-ion batteries.