Unveiling the Crucial Role of Dissolved Fe2+ on the Solid Electrolyte Interphase in Long‐life LiFePO4/Graphite Batteries
Shijun Tang,Yuli Liang,Yufan Peng,Yonggang Hu,Yiqing Liao,Xuerui Yang,Huiyan Zhang,Ying Lin,Ke Zhang,Jinding Liang,Bowen Li,Guangjin Zhao,Yimin Wei,Zhengliang Gong,Yong Yang
DOI: https://doi.org/10.1002/aenm.202402842
IF: 27.8
2024-09-01
Advanced Energy Materials
Abstract:The impact of transition metal Fe2+ on the dynamic solid electrolyte interface (SEI) in long‐life LiFePO4/Graphite batteries is comprehensively and quantitatively investigated. At elevated temperatures, dissolved Fe2+ tends to deposit on the anode, leading to an increase in organic components, particularly lithium alkyl carbonates, within the SEI. This process accelerates the consumption of active lithium and capacity degradation. The dissolution of iron from the cathode significantly contributes to the accelerated degradation of LiFePO4/Graphite batteries, particularly at elevated temperatures. However, a systematic understanding of the spatial distribution and impact of Fe ions on the dynamic solid electrolyte interphase (SEI) layer is lacking. In this study, a comprehensive and quantitative investigation is conducted into the effects of transition metals (TM) and thoroughly examined the interaction between dissolved Fe2+ and SEI in long‐life LiFePO4/Graphite pouch cells. The dissolved Fe in the electrolyte is more prone to deposition at the negative electrode at elevated temperatures, leading to an accelerated loss of active lithium. Additionally, Fe deposition on the SEI catalyzes the decomposition of EC and contributes to an increase in organic components, particularly lithium alkyl carbonates within the SEI, as evidenced by mass spectrometry titration (MST) analysis. Neutron imaging (NI) provides more insights into the impacts of dissolved Fe2+ on active lithium loss, SEI components, and electrolyte decomposition, resulting in greater macroscopic heterogeneity in the electrode regions of the cells. This research sheds light on the mechanisms underlying the degradation of LiFePO4/Graphite batteries and provides valuable insights for the development of strategies to mitigate capacity fade and enhance battery performance and longevity.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,energy & fuels