Enhanced Photoluminescense of Gd2O3∶ Sm3+ Nanocrystals by Li+ Doping
Xue YU,Hai-gang XU,Jiang YIN,Wei-feng ZHANG
2007-01-01
Chinese Journal of Luminescence
Abstract:The luminescence properties of nanosized lanthanide oxide materials have attracted extensive inte- rest because of their fundamental and technological importance.Gd_2O_3,which is easily obtained due to abun- dant resource in nature,has been widely used as host material.The emission efficiency of Sm~(3+) associated with the intra-4f-shell transition is very high,and it earl emit bright light under both ultraviolet and infrared excitation.Therefore,it often plays a very important role in many luminescent materials.In this paper, Gd_2O_3:Sm~(3+) and Li~+-doped Gd_2O_3:Sm~(3+) nanocrystals were prepared by a combustion method.The pure nanocrystals were obtained after annealing at 800℃,and the crystallinity was improved with increasing annea- ling temperature.Both Gd_2O_3:Sm~(3+) and Li~+-doped Gd_2O_3:Sm~(3+) nanocrystals appeared to be cubic crystal- line phase according to the XRD results.In contrast to Gd_2O_3:Sm~(3+) which showed an irregular shape of ag- glomerated fine particles,the morphology of Li~+-doped Gd_2O_3:Sm~(3+) nanocrystals were spherical and quite regular.These particles were measured to be about 50 nm in diameter.When excited at 275 nm and 980 nm, Gd_2O_3:Sm~(3+) and Li~+-doped Gd_2O_3:Sm~(3+) nanocrystals exhibit similar emission spectra,which consist of the characteristic emission bands of the Sm~(3+) ions (~4G_(5/2)→~6H_J,J=5/2,7/2,9/2 transitions at 560,602,650 nm in the spectra) due to an efficient energy transfer from the Gd_2O_3 host lattice to the doped Sm~(3+) ions.It was found that the incorporation of Li~+ into the Gd_2O_3:Sm~(3+) nanocrystals has greatly enhanced the photolumi- nescence intensity of Sm~(3+) in both photoluminescence and upconversion emission.The highest emission inten- sity was observed with Gd_(1.83)Li_(0.15)Sm_(0.02)O_3,whose brightness was increased by a factor about 7.0 in compari- son with that of Gd_2O_3:Sm~(3+).As we all known that defects of the surface of the nanoparticles,which provide non-radiation recombination routes for electrons and holes,often act as non-radiative centers and has great in- fluence on luminescent properties.It can be suggested that the incorporation of Li~+ can greatly decrease the deficiencies and oxygen vacancies.That is,the defects and oxygen vacancies of the surface of nanoparticles decreased at first when Li~+ content was lower,which decreased the luminescence quenching centers and in- creased the crystallinity,thereby enhanced the emission intensity.A lot of defects could be induced in the sys- tem with a gradual increase of Li~+ content.This will destroy the crystallinity and thus lead to the luminescence quenching.In conclusion,this paper reported the correlation between the morphology,structure and optical behaviors on Gd_2O_3:Sm~(3+) nanocrystals doped with Li~+ Li~+ doping at a low content significantly improved the morphology of phosphors and strongly enhanced the luminescent properties.