Bidisperse Magnetorheological Fluids with Strong Magnetorheological Response, Long-term Stability and Excellent In-use Performance

Mona Nejatpour,MOSTAFA KHALIL ABDOU SALEH,Abasin Ulasyar,Ugur Unal,ismail lazoglu,Havva Funda Yagci Acar
DOI: https://doi.org/10.1088/1361-665x/ad1e8a
IF: 4.1
2024-01-17
Smart Materials and Structures
Abstract:There is a critical demand for Magnetorheological Fluids (MRFs) with high particle loading, long-term stability, and high magneto-viscous properties to be used in industrial MRF devices. Bidisperse MRFs composed of highly magnetizable micron-sized carbonyl iron (CI) particles and poly(acrylic acid) coated superparamagnetic iron oxide nanoparticles (SPION-PAA) that can chemically interact are proposed to achieve such MRFs, here. Coating bare, commercial CI with lauric acid (LA) enhanced its dispersibility in a hydrophobic carrier fluid, allowed high magnetic loading and significantly prevented the sedimentation of the particles when mixed with 9-12 wt% SPION. Different carrier fluids (mineral oil, paraffin, and hydraulic oil) were tested and hydraulic oil was determined as the best for this particle combination. The most stable bidisperse MRF was achieved at 83-84% magnetic content with 12 wt-%SPION-PAA, LA-coated-CI and 3 wt% polyvinyl alcohol (PVA). Such MRFs outperformed the commercial benchmark, 140-CG® from Lord Corp., in long-term stability (4 months) and stability under dynamic loading. Bidisperse MRFs were stable between 20-60 °C. Most importantly, the excellent performance of the bidisperse MRFs in dampers designed for washing machines suggests that these MRFs may provide comparable damping forces with much better stability, ensuring longer shelf-life and longer lifetime in use.
materials science, multidisciplinary,instruments & instrumentation
What problem does this paper attempt to address?
### Problems the paper attempts to solve The paper aims to solve the problems of magnetorheological fluids (MRFs) in terms of high magnetic particle loading, long - term stability and high magnetoviscous properties. Specifically, the paper proposes bidisperse MRFs, which are composed of highly magnetized micron - sized carbonyl iron (CI) particles and superparamagnetic iron oxide nanoparticles (SPION - PAA) coated with polyacrylic acid, in order to achieve these goals. ### Main research contents 1. **Improving stability**: - Through tests using different carrier liquids (mineral oil, paraffin oil and hydraulic oil), hydraulic oil was determined as the best carrier liquid. - By coating lauric acid (LA) on the surface of CI particles, their dispersibility in hydrophobic carrier liquids was enhanced, and particle sedimentation when mixed with 9 - 12 wt% SPION was significantly prevented. - A small amount of polyvinyl alcohol (PVA) was added as a stabilizer to further improve the stability of MRFs. 2. **Improving magnetorheological properties**: - The magnetorheological responses of bidisperse MRFs with different compositions were studied, especially their performance under high particle loading. - The properties of magnetic particles were evaluated by characterization methods such as dynamic light scattering (DLS), transmission electron microscopy (TEM), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). 3. **Practical applications**: - The long - term stability (4 months) and stability under dynamic loading of bidisperse MRFs were compared with the commercial benchmark 140 - CG®. - The performance of bidisperse MRFs in washing machine shock absorbers was tested, and the results showed that they had better stability and comparable damping force. ### Key results - **Optimal formula**: Bidisperse MRFs containing 12 wt% SPION - PAA, LA - coated CI and 3 wt% PVA showed the best stability at a magnetic content of 83 - 84%. - **Long - term stability**: Bidisperse MRFs remained stable within 4 months, which was better than the commercial benchmark 140 - CG®. - **Temperature stability**: Bidisperse MRFs remained stable in the range of 20 - 60°C. - **Practical application**: In washing machine shock absorbers, bidisperse MRFs showed better stability and comparable damping force, ensuring a longer shelf life and service life. ### Conclusion This research has successfully developed a bidisperse MRFs with high magnetic particle loading, long - term stability and high magnetorheological properties, providing a new option for industrial magnetorheological devices.