Highly exposed surface pore-edge FeNx sites for enhanced oxygen reduction performance in Zn-air batteries

Xiangyu Lu,Lihui Xiao,Peixia Yang,Hao Xu,Lilai Liu,Ruopeng Li,Yaqiang Li,Huiling Zhang,Jinqiu Zhang,Maozhong An
DOI: https://doi.org/10.1039/d2qi02228a
IF: 7.779
2022-12-16
Inorganic Chemistry Frontiers
Abstract:Single Fe atom with N-coordination (FeN x sites) in Fe-N-C catalysts are widely recognized as the active centers for catalyzing oxygen reduction reaction (ORR), but attaining superior intrinsic activity and the more expose of FeN x sites remains challenging. Herein, a surface pore-edge FeN x sites anchored on suitable porous carbon (SPE-FeN x -HPNC) is reported, which simultaneously enhances intrinsic activity and more exposed active sites for ORR. Theoretical calculations suggest that pore-edge FeN x sites are more active than pure FeN x sites in the rate-determining step, hence promoting the intrinsic ORR activity of active sites. Therefore, due to the abundant surfcace pore-edge FeN x sites and beneficial pore structures, SPE-FeN x -HPNC exhibits the ecellent ORR activty with a half-wave potential ( E 1/2 ) of 0.902 V in alkaline medium. Moreover, the assembled Zn-air battery with SPE-FeN x -HPNC delivers a peak power density of 150 mW cm -2 and a durable charge-discharge cycle over 450 hours. This work would provide a effective strategy for preparing high-performance catalyst for Zn-air batteries.
chemistry, inorganic & nuclear
What problem does this paper attempt to address?