Abstract:The mixture of Pluronic F108 (EO 132 PO 50 EO 132 ) and P104 (EO 27 PO 61 EO 27 ) surfactants combined with toluene (swelling agent) templates ethylene-bridged organosilica nanotubes, whose size is widely adjustable by changing the initial synthesis temperature. While nanotubes of inner diameters ∼11 nm formed at room temperature, the temperature decrease led to the size increase and afforded nanotubes of particularly large inner diameters (from 25 to ∼35–40 nm) and thick walls at 7.5–9.25 °C, with outer diameters reaching ∼80 nm. The thick walls make these nanotubes resistant to collapse and suppress the nanotube aggregation. The stirring rate during the initial stage of the synthesis was an important factor in determining the uniformity and size of the ultra-large-diameter nanotubes. Slow stirring may lead to thin-walled organosilica nanotubes with outer diameters above 80 nm, showing that such structures can form, but their content and diameter uniformity were low. Our results suggest that the tubular soft-templating system transitions from the swollen micelle regime to the microemulsion regime, in which the inner core consists of the swelling agent only. In the latter case, the inner diameter of the surfactant-templated nanotubes, which is expected to be related to the size of the hydrophobic domain, may be enlarged to 35–40 nm (for good-quality products) or even beyond 40 nm (for low-purity products). Methylene-bridged organosilica nanotubes with tunable diameters, including very large ones, were also obtained, suggesting a broader scope of our pore diameter adjustment approach. Ethenylene- and xylylene-bridged organosilica nanotubes were also synthesized, indicating a wide applicability of our templating system.

Controlling Wall Thickness of Silica Nanotubes Within 4-Nm Precision

A Facile Method to Fabricate Silica-Coated Carbon Nanotubes and Silica Nanotubes from Carbon Nanotubes Templates

Large-scale Controlled Synthesis of Silica Nanotubes Using Zinc Oxide Nanowires As Templates

Preparation of Aluminosilicate Ferrierite Zeolite Nanosheets with Controllable Thickness in the Presence of a Sole Organic Structure Directing Agent

Fabrication and Characterization of Silica Nanotubes with Controlled Dimensions

Gram-Scale Synthesis of Silica Nanotubes with Controlled Aspect Ratios by Templating of Nickel-Hydrazine Complex Nanorods

Synthesis of Silica Nanocubes by Sol–gel Method

Kinetically-controlled template-free synthesis of hollow silica micro-/nanostructures with unusual morphologies.

Synthesis of bridged-organosilica nanotubes with widely adjustable inner diameter based on temperature-dependent templating by swollen mixed surfactant micelles

Assembled pentasil nanosheet zeolites: Adjusting the sheet thickness through a simple and direct dual templating approach

Mechanistic Insight into the Synthesis and Morphological Evolution of Superhydrophobic Silica Nanotubes

Tunable One-Dimensional Helical Nanostructures: from Supramolecular Self-Assemblies to Silica Nanomaterials

Synthesis and Characterization of Silica Nanotubes with Radially Oriented Mesopores

Controllable Preparation Of Ultra-Low-Dielectric Nanoporous Silica Via Inorganic-Organic Hybrid Templates

Self-catalytic Sol-Gel Synergetic Replication of Uniform Silica Nanotubes Using an Amino Acid Amphiphile Dynamically Growing Fibers As Template.

Synthesis of well-defined silica and Pd/Silica nanotubes through a surface sol-gel process on a self-assembled chelate block copolymer

Controlled Synthesis of Tellurium Nanostructures from Nanotubes to Nanorods and Nanowires and Their Template Applications

Subnanometer Diameter Control in Nanotubes Self‐Assembled via Consecutive Cyclization – Polymerization Processes

Structural control of mesoporous silicas with large nanopores in a mild buffer solution

Silica nanotubes synthesized from TEOS with ammonium D,L-tartrate as template and their characterization

The Size-Controllable Synthesis of Nanometer-Sized Mesoporous Silica in Extremely Dilute Surfactant Solution