Abstract:The effect of coating cracking during depth-sensing indentation testing (e.g. nanoindentation testing) on systems comprising thin hard coatings (e.g. TiN) on a less stiff, hard substrate (e.g. steel) has been investigated in order to establish whether, at such small scales, the occurrence of annular through-thickness cracks around indentation sites can be detected from load–displacement plots and whether any accompanying localized debonding of the coating from the substrate can also be identified. Experiments were performed on thin TiN and NbN monolayers, and compositionally modulated TiN/NbN and TiN/ZrN deposited onto hard steel or stainless steel substrates. Above a critical load (Pcrit) in the range 80–500mN, all systems exhibited annular through-thickness cracks around indentation sites. The cracking was found to be accompanied by a discrete change in gradient of the loading portion of the load–displacement curve. Also, analysis of the unloading curves beyond this point showed that elastic recovery was controlled by the elastic modulus of the underlying substrate material alone. The cracking mechanism has been characterized using scanning electron microscopy, coupled with optical profilometry to map the detailed z-displacement of the surface — a procedure critical to understanding whether coating–substrate debonding had occurred. Some cracks were found to show a spiral morphology and the effect of indentation loading rate was investigated to see if appearance of these cracks was loading-rate sensitive. Our results highlight the problems inherent in assessing both the interfacial failure and the interfacial fracture toughness of thin film coated systems at the small contact scales (⩽1μm) associated with crack genesis where it is difficult to confirm the extent of sub-surface cracks by conventional means. We have also demonstrated that both load–displacement and load–displacement squared plots are necessary if a more complete understanding of system behaviour is to be gained. Also, a simple fracture mechanics model for the annular cracking behaviour seen in such systems has been derived and used to estimate a value of Gic (the interfacial work of fracture) as 180Jm−2 for the TiN/ZrN-stainless steel system.

The Transient Response of a Coating–substrate Structure with a Crack in the Functionally Graded Interfacial Layer

Finite Element Analysis of Crack Dynamic Response in Gradient Non- Homogeneous Finite Plate

Transient Response of Multiple Interface Cracks in Fine-Grained Coating Composite Structures under Impact Loading

Interaction between rectangular cracks embedded in infinite medium

Crack Problems for Functionally Graded Materials under Transient Thermal Loading

Influence of FGM coating on the dynamic fracture behavior of multiple cracks in a homogeneous half-plane under in-plane loading

Dynamic Stress Intensity Factors of a Semi-Infinite Crack in an Orthotropic Functionally Graded Material

Fracture Analysis of Griffith Interface Crack in Fine-Grained Piezoelectric Coating/Substrate under Thermal Loading

Dynamic Thermal Response of Multiple Interface Cracks between a Half-Plane and a Coating Layer under General Transient Temperature Loading

Cracks problem for non-homogeneous composite material subjected to dynamic loading

Transient response of an interface crack between dissimilar piezoelectric layers under mechanical impacts

Dynamic mode III stress intensity factors of multiple axisymmetric interfacial cracks in an FGM coated orthotropic layer

Influences of Interface Properties and Coating Thickness on Fracture Behaviors of Coating/substrate Systems

Dynamic Response for Functionally Graded Materials with Penny-Shaped Cracks

The effect of coating cracking on the indentation response of thin hard-coated systems

Three-dimensional tractive rolling contact analysis of functionally graded coating-substrate systems with interfacial imperfection and frictional anisotropy

Multiple crack problem in nonhomogeneous composite materials subjected to dynamic anti-plane shearing

Partial slip contact of materials with vertically aligned cracks near surface

Investigation into the Dynamic Fracture Properties of Large Scale Functionally Graded Materials

Interactions of Three Parallel Square-Hole Cracks in an Infinite Plate Subjected to Internal Pressure

Interaction of an interfacial crack with linear micro-defects under out-of-plane shear loading