Phase Transition and Temperature Dependences of Electrical Properties of [Bi0.5na1-X-ykxliy)(0.5)]tio3 Ceramics

Y Yuan,SR Zhang,XH Zhou,JS Liu

DOI: https://doi.org/10.1143/jjap.45.831

IF: 1.5

2006-01-01

Japanese Journal of Applied Physics

Abstract:Lead-free piezoelectric ceramics [Bi0.5(Na1-x-yKxLiy)0.5]TiO3 (abbreviated BNT–BKT–BLT) were prepared by the conventional oxide method. The effects of BKT and BLT amounts on the phase transition and electrical properties were examined. BNT–BKT–BLT ceramics give good performances with piezoelectric constant d33=216 pC/N and planar electromechanical coupling factor kp=40.1% at 20 mol % BKT with a fixed BLT amount of 10 mol %. Also, the optimal d33 of 173 pC/N and kp of 38.0% are obtained at 10 mol % and 7.5 mol % BLT, respectively when the BKT amount is 17.5 mol %. The addition of BKT reduces the depolarization temperature Td, however, it increases the Curie temperature Tc. In contrast, Td and Tc are shifted towards a higher temperature with increasing amount of BLT. BNT–BKT–BLT ceramics show typical ferroelectric features at room temperature. The addition of BKT increases the remnant polarization Pr and lowers the coercive field Ec significantly. The polarization–electric field (P–E) hysteresis loops at different temperatures reveal that the loops deform at a high temperature as a result of the phase transition from ferroelectric to antiferroelectric during the heating process, so that d33 diminishes rapidly.