Abstract:In this study, a facile strategy is reported for the preparation of porous carbon materials with adjustable pore size through carbonization of MOF-5 at 900 degrees C with the assistance of different additives. Results show that the physical and chemical properties (such as morphology, carbon defect content, BET specific surface area, pore structure) of the porous carbon materials can be adjusted through introduction of different compounds (i.e., C16H32O2, C6H14O6, C18H36O2, Na2CO3, KOH, Cu(NO3)2, NaCl, KCl, MgCl2, ethyl cellulose) during the carbon-ization processes. CO2 adsorption experiment results show that there is a linear relationship between the CO2 adsorption capacity (at 25 degrees C and 0.15 bar) and the cumulative pore volume of pores at 5-7 angstrom, suggesting that pores in the range of 5-7 angstrom play a major role in CO2 adsorption at such condition. While the CO2 adsorption capacity (at 25 degrees C and 0.15 bar) is independent on the BET specific surface area of the materials. Among the prepared porous carbon materials, 5C-C6H14O6-900 exhibits the highest CO2 adsorption capacity (i.e., 3.32 mmol/g at 25 degrees C and 1 bar, 0.88 mmol/g at 25 degrees C and 0.15 bar), with good adsorption/desorption cycle stability and CO2/N2 selectivity. Our work provides a facile and general method to adjust and control the pore size dis-tribution of MOF-derived porous carbon materials. Besides, the analysis results indicate that the micropores in a specific pore size range play a decisive role in the adsorption of CO2 at low pressure, which provides a new idea for the preparation of high-efficiency adsorbents at low pressures.

Mesoporous Carbon Materials Prepared from Carbohydrates with A Metal Chloride Template

Facile synthesis of ordered mesoporous carbon with finger citron residue as carbon precursor

Sio2-Template Synthesis of Mesoporous Mgf2 Highly Effective for Cl/F Exchange Reaction

Design of Carbon Materials with Ultramicro-, Supermicro- and Mesopores Using Solvent- and Self-Template Strategy for Supercapacitors

Mesoporous Carbon Materials: Synthesis and Modification.

Synthesis of Mesoporous Carbon Using Halloyiste As Template

Facile Synthesis of MOF-5-derived Porous Carbon with Adjustable Pore Size for CO2 Capture

Preparation of Porous Carbons from Halloysite-Sucrose Mixtures

Preparation of mesoporous carbons by a template method

Facile preparation of hierarchically porous carbons from metal-organic gels and their application in energy storage

Preparation of hierarchical porous carbons from sodium carboxymethyl cellulose via halloysite template strategy coupled with KOH-activation for efficient removal of chloramphenicol

Facile Synthesis of Hierarchically Porous Carbons from Dual Colloidal Crystal/Block Copolymer Template Approach

Facile Synthesis of Hierarchically Macro/Mesoporous Carbons by Polymerization-Induced Phase Separation Combined with Starch Template

Zeolitic Type Templated Porous Carbon Materials

Nitrogen-containing Mesoporous Carbons Prepared from Melamine Formaldehyde Resins with CaCl2 As a Template.

Building Metal-functionalized Porous Carbons from Microporous Organic Polymers for CO2 Capture and Conversion under Ambient Conditions

From metal-organic framework to nanoporous carbon: toward a very high surface area and hydrogen uptake.

Controlled Synthesis Of Ordered Mesoporous Carbohydrate-Derived Carbons With Flower-Like Structure And N-Doping By Self-Transformation

Preparation and application performance study of biomass-based carbon materials with various morphologies by a hydrothermal/soft template method

Coordinative template catalyzed/templated nanocarbon with ultrahigh mesoporosity for high-performance aqueous supercapacitor

Synthesis and characterization of microporous carbons templated by ammonium-form zeolite Y