Abstract:Mesoporous carbon materials with ultra-thin carbon pore walls and highly dispersed Ni nanoparticles have been successfully prepared by using two different SBA-15 silicas as hard templates and 2,3-dihydroxynaphthalene (DHN) as a carbon precursor. The nickel precursor was a concentrated nickel nitrate hexahydrate [Ni(NO3)(2)center dot 6H(2)O] solution in 2-propanol, which was added to the carbon-silica nanocomposite prior to thermal treatment. The samples studied were analyzed by thermogravimetry (TG), nitrogen adsorption at -196 degrees C, powder X-ray diffraction (XRD), Raman spectroscopy, scanning and transmission electron microscopy (STEM), and in situ electron diffraction X-ray spectroscopy (EDX). While TG analysis revealed carbon contents lower than 30 wt.-%, nitrogen adsorption provided information about the homogeneity of the carbon thin film deposited onto the mesopore walls of the ordered silica templates SBA-15. The templates, carbon-silica nanocomposites, and carbon inverse replicas with nickel nanoparticles exhibit uniform pores, high surface areas, and large pore volumes. Partially graphitic carbon was identified by the presence of a characteristic G band in the Raman spectra, whereas the diffraction peak attributed to the stacking of graphene planes was not observed by powder XRD. The presence of ordered domains in the carbon materials studied was confirmed by small angle XRD and STEM imaging. In addition, the STEM images revealed that the nickel nanoparticles are uniform in size, ca. 3 nm, and are homogeneously dispersed on the tubular carbon walls. A few larger clusters of nickel, ca. 60 nm, present on the external surface, were identified by powder XRD as metallic Ni. The in situ EDX revealed that the small nanoparticles are largely composed of Ni with traces of NiO. Similar nanoparticle dispersions have been reported only for Ni-containing multiwalled carbon nanotubes (CNTs), whereas previously reported ordered mesoporous carbon materials, CMK-3, possess larger Ni/NiO nanoparticles. ((C) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2009)

Carbon Nanohorns Hybridized with a Metal-Included Nanocapsule

Large-scale Synthesis of Single-Walled Carbon Nanohorns by Submerged Arc

Boosting the Performance of the Fe–N–C Catalyst for the Oxygen Reduction Reaction by Introducing Single-Walled Carbon Nanohorns As Branches on Carbon Fibers

Nickel Nanoparticles Embedded in Porous Carbon-Coated Honeycomb Ceramics: A Potential Monolithic Catalyst for Continuous Hydrogenation Reaction

Synthesis and Characterization of Cu Filled Carbon Nanohorns

Scalable Production of Carbon Encapsulated Ni Nanoparticles by Water Arc Discharge: Structural and Magnetic Properties

The effect of carbon encapsulation on the magnetic properties of Ni nanoparticles produced by arc discharge in de-ionized water

Pentadiamond-like Metallic Hard Carbon Nitride

Synthesis of single-wall carbon nanohorns by arc-discharge in air and their formation mechanism

Formation and subsequent inclusion of fullerene-like nanoparticles in nanocomposite carbon thin films

Synthesis and catalytic activity of heteroatom doped metal-free single-wall carbon nanohorns.

Size Controllable Metal Nanoparticles Anchored on Nitrogen Doped Carbon for Electrocatalytic Energy Conversion

Mesoporous Carbon Materials with Ultra‐Thin Pore Walls and Highly Dispersed Nickel Nanoparticles

Copper induced hollow carbon nanospheres by arc discharge method: controlled synthesis and formation mechanism

Polymerized Carbon Nitride Nanobells

Single-walled carbon-nanohorns improve biocompatibility over nanotubes by triggering less protein-initiated pyroptosis and apoptosis in macrophages

Preparation of carbon-encapsulated alloy nanomaterials by detonation decomposition of nitrate complex explosives containing multi-metallic ions

Formation of a Highly Reactive Cobalt Nanocluster Crystal Within a Highly Negatively Charged Porous Coordination Cage.

Electronic and Structural Properties of Carbon Nano-Horns

Synthesis,Characterization and Performance of Helical Carbon Nanotubes

A Practical Route to the Production of Carbon Nanocages