Improving Mechanical and Magnetocaloric Responses of Amorphous Melt-Extracted Gd-based Microwires Via Nanocrystallization
H. F. Belliveau,Y. Y. Yu,Y. Luo,F. X. Qin,H. Wang,H. X. Shen,J. F. Sun,S. C. Yu,H. Srikanth,M. H. Phan
DOI: https://doi.org/10.1016/j.jallcom.2016.08.254
IF: 6.2
2016-01-01
Journal of Alloys and Compounds
Abstract:We report on the structural, mechanical, and magnetocaloric properties of annealed melt-extracted Gd53Al24Co20Zr3 amorphous microwires of similar to 70 mm diameter. During heat treatment small islands of nanocrystallities are generated and isolated in the amorphous region for the wires. The size of the nanocrystallities ranges from 5 nm to 10 nm. The observed lattice distortion from the nanocrystallities causes changes in the magnetic properties of the wires. The annealing temperature of 100 degrees C has the largest strength (1845 MPa) as compared to wires annealed at other temperatures. This is likely to trigger nanophase transformation in the amorphous region and these nanocrystals have been preserved through the increase of annealing temperature. The formulation of the nanocrystalline islands is also verified by the selected-area electron diffraction (SAED). The microwires exhibit a large and reversible magnetocaloric effect (MCE), with the maximum isothermal magnetic entropy change (-Delta S-M) and refrigerant capacity (RC) values of 9.5 J/kg K and 689 J/kg respectively for the microwire annealed at 100 degrees C. This RC is about 35%, 67%, and 91% larger than those of bulk Gd53Al24Co20Zr3 (similar to 509 J/kg), Gd (-410 J/kg), and Gd5Si2Ge1.9Fe0.1 (similar to 360 J/kg) regardless of their ordering temperatures. These results demonstrate the ability to tune the mechanical and magnetic properties of the microwires by thermal annealing. (C) 2016 Elsevier B.V. All rights reserved.