Abstract:Ferric ions present in an acidic aqueous suspension of TiO2 can promote significantly the photocatalytic degradation of a textile dye X3B upon UV light irradiation (λ ≥ 320 nm). The initial rate of X3B degradation was observed to increase exponentially with the initial concentration of Fe(III). However, this enhancement disappeared as all ferric species were transferred into ferrous ions, and after that the degradation of X3B proceeded via a regular pathway of photocatalysis. Several control experiments revealed that the beneficial effect of Fe(III) was attributed mainly to electron trapping at the semiconductor surface, whereas the contribution from homogeneous Fe(III) photolysis, capable of producing hydroxyl radicals, was not significant. In the liquid phase, more than 98.2% of Fe(II) was detected, implying that the involvement of (Photo)-Fenton reaction was less possible. On the other hand, the ferrous ion, once produced, exhibited no obvious effect on X3B degradation, but its formation became faster in the presence of X3B, suggesting that hole oxidation of X3B might be involved as well. Both Fe(III) and X3B were adsorbed strongly on the catalyst surface, allowing efficient separation and utilization of the electron-hole pairs, whereas Fe(II) was hardly adsorbed, which probably was one of the reasons that Fe(II) could not be re-oxidized in situ by hole or other reactive species generated in the system. Moreover, the increase in the initial pH from 1.6 to 3.7 did not affect obviously the initiate rate of X3B degradation, but led to significant decrease in the initial rate of Fe(II) formation. Together with the exponential increase of Fe(II) formation rate with initial Fe(III) concentration, the primary evidence suggests that the efficiency of electron trapping by Fe(III), similar to Fe(III) photolysis, is also dependent of ferric species polymerization on the surface. The results obtained in this work will be relevant to the study on Fe-doped photocatalyst.

Photocatalytic degradation of textile dye X3B by heteropolyoxometalate acids.

Photocatalytic Degradation of Textile Dye X-3b Using Polyoxometalate-Tio2 Hybrid Materials

Reaction Mechanism on the Synergistic Photodegradation of Dye X3B and Photoreduction of Dichromate in the Presence of Polyoxometalate

Study of ultraviolet-assisted the combination of hydrogen peroxide and potassium ferrate on X-3B degradation efficiency

Photothermal Effect Improving the Activity of Spinel MnFe2O4 Nanoparticles for the Catalytic Activation HCO3−/H2O2 to Achieve the Degradation of Dye Pollutants in Low-Temperature Condition

Degradation of Reactive Brilliant Red X-3B by Photo-Fenton-like Process: Effects of Water Chemistry Factors and Degradation Mechanism

Synthesis of Ternary Hybrid TiO2-SiO2-POM Catalysts and Its Application in Degrading Rhodamine B under Visible Light Illumination

Efficient degradation of dye pollutants on nanoporous polyoxotungstate–anatase composite under visible-light irradiation

Comparative studies of the Fe3+/2+-UV, H2O2-UV, TiO2-UV/vis systems for the decolorization of a textile dye X-3B in water.

Effects of Polyoxometalate and Fluoride on Adsorption and Photocatalytic Degradation of Organic Dye X3b on Tio2: the Difference in the Production of Reactive Species

Photocatalytic degradation of textile dye X-3B using TiW11Ti/SiO2 hybrid materials

Photoelectrocatalytic degradation of triazine-containing azo dyes at γ-Bi2MoO6 film electrode under visible light irradiation (λ > 420 Nm)

Synergistic Photosensitized Removal of Cr(VI) and Rhodamine B Dye on Amorphous TiO2 under Visible Light Irradiation.

Photocatalytic Degradation of Organic Dyes with Er3+:YAlO3/ZnO Composite under Solar Light

Uv- Or Visible-Light-Induced Degradation Of X3b On Tio2 Nanoparticles: The Influence Of Adsorption

Photocatalytic Degradation of Organic Dyes by a High Efficient TiO<sub>2</sub>-Based Catalysts Under Solar Light Irradiation

Photocatalytic degradation of selected dyes by titania thin films with various nanostructures

Highly Efficient Photodegradation of RhB–MO Mixture Dye Wastewater by Ag3PO4 Dodecahedrons under Acidic Condition

Photo-assisted degradation of Rhodamine B by a heterogeneous Fenton–like process: performance and kinetics

Reaction mechanism of Fe(III) participated photocatalytic degradation of X3B over TiO2

Polyoxometalate-mediated Reduction of Dichromate under UV Irradiation