Abstract:Ethylenediamine-doped (EDA-doped) polyaniline (PANI) films were deposited via spin coating technique on a glass substrate. The samples were annealed at different times and temperatures. The characterizations of the prepared PANI films were described by X-ray diffraction (XRD), transmission electron microscopy (TEM), and Fourier transform infrared spectroscopy (FT-IR). It is found that the conductivity changes under deep mouth exhaling for 150/1 h sample is 1.65 times faster than the films annealed at 100°C/4 h. The response and recovery time of the 150/1 h EDA-doped PANI film is decreased by order of 0.63 and 1.29 s than those films dried at 100°C for 4 h, respectively. The 150/1 h EDA doped PANI film during deep exhaling its conductivity increased abruptly from 2.2 × 10 –7 to 0.026 S/cm –1 . In a few seconds, following an inhalation, there occurs a complete transition to the dry state conductivity. Furthermore, the increment in conductivity of the EDA-doped PANI films was determined at various RH levels (20, 40, 60, 80, and 90%) with exposure and evacuation of the humid air. The doped PANI sample annealed at 150°C for 1 h exhibit the highest conductivity at 90% RH. The conductivity was increased from 2.16 × 10 –7 S/cm for the insulating state at the dry state to 0.23 S/cm for the semiconducting state at 90% RH. Consequently, the 150/1 h sample showed an increase in conductivity by order of 10 6 at 90% RH. For all samples, the conductivity progressively rises as the RH value increases till 90% of RH value samples exhibit an abrupt increase in conductivity except the 100°C/4 h sample. The highest conductivity is 0.041 S/cm at 90% RH obtained for the case of 150/30 min sample, whereas the 150/1 min and 100/4 h films show maximum conductivity of 0.027 and 0.007, respectively.

Synthesis and humidity sensitivity of conducting polyaniline in SBA-15

HUMIDITY SENSITIVE PROPERTIES OF WATER SOLUBLE POLYANILINE

Water-soluble polyaniline and its composite with poly(vinyl alcohol) for humidity sensing

The Electrical Responses to Humidity of a Composite of Polyaniline and Polyelectrolyte

Synthesis of Polyaniline/mcm‐41 Composite Through Surface Polymerization of Aniline

Encapsulation of Polyaniline in 3-D Interconnected Mesopores of Silica KIT-6.

Electrospun nanofibers of polymer composite as a promising humidity sensitive material

Highly Sensitive and Ultrafast Response Surface Acoustic Wave Humidity Sensor Based on Electrospun Polyaniline/poly(vinyl Butyral) Nanofibers.

Investigations on the sensing mechanism of humidity sensors based on electrospun polymer nanofibers

Polyaniline Nanofiber Humidity Sensor Prepared by Electrospinning

Preparation and characterization of polyaniline with high electrical conductivity

Preparing and Conductivity Properties of Polyaniline/polybenzobisoxazole Composites

Synthesis, DSC Properties, Surface Morphology and the Third-Order Behavior Studies of a Conducting Polymer

Thermal Conductivity Measurements on Pani/Sba-15 and Ppy/Sba-15

Synthesis, characterization, and humidity sensing performance of polyaniline bismuth-doped zinc oxide (PANI-Bi-ZnO) composites

Investigation of Insulator-to-Semiconductor Fast Transition in Sheet-Like Polyaniline Films

Synthesis and Structural Characterization of Polyaniline/Mesoporous Carbon Nanocomposite

The frequency-dependence conduction of polyaniline based on their para-crystalline structures

Resistivity study of polyaniline doped with protonic acids

Electrical and Structural Analysis of Conductive Polyaniline/polyacrylonitrile Composites

Ab Initio Studies of the Differences in the Chemical Reactivity and Electronic Properties of Polyaniline and Its Derivatives