The feasibility of repairing abdominal wall defects by designed biodegradable composite scaffold

LIU Zheng-ni,TANG Rui,ZHOU Zhi-yuan,GU Yan

2010-01-01

Abstract:Objective This study is designed to investigate the feasibility of repairing abdominal wall defects by biodegradable composite scaffold constructed by us with polylactic acid,chitin and gelatin.Methods Natural gelatin was cross-linked through 1% glutaraldehyde as the internal biodegrad-able scaffold.Polylactic acid was mixed with chitin in the ratio of 7∶1 to fabricate the external mesh.Then,the gelatin mesh was inserted into the external mesh.The degradation time of the scaffold was observed through immersion into the PBS solution.Direct contact and MTT were used to detect the cytotoxicity;mechanical properties were measured through stretching and bursting load tests,cell adhesion,proliferation,differentiation and collagen secretion status were observed by seeding 1×107 cell/mL fibroblasts on the scaffold.Results The degradation time of cross-linked gelatin was(54.8±0.5) days,which could meet the demands of early degradation after cell ingrowth.The degradation time of external mesh was(312.5±6.5) days,which could help maintaining long-term strength during tissue regeneration.The transversal fracture strength of the external mesh was(319.2±37.8)N,and its vertical fracture strength was(620.4±45.2)N,both were adequate for abdominal wall defects repairing.Cytotoxicity test of the scaffold demonstrated that it belonged to grade 0-1;and the fibroblasts proliferated well on the scafold;there was no statistically significant difference as compared with the control group(P>0.05).The scaffold had been covered fully by fibroblasts after seeding and mixed culturing for 5 days.Light microscope showed that the fibroblasts started secreting extracellular stroma from the 7th day.Conclusions We applied cross-linked gelatin as the internal scaffold and fabricated polylactic acid-chitin mixture as the external mesh to construct the biodegradable composite scaffold.The scaffold is totally degrable and biocompatible.Furthermore,it possesses good mechanical properties.The properties of the scaffold in vitro meet the requirements for usage in repairing abdominal wall defects.