Corrosion Resistance of Ti-Pd Coating Prepared on Titanium Substrate by Glow Plasma Surface Metallurgy Process

Li Zhengxian,Hu Tao,Liu Daoxin,Wang Shaopeng,Du Jihong,Xu Zhong,Zhou Lian
2008-01-01
Rare Metal Materials and Engineering
Abstract:Ti-Pd alloying coating was prepared on the surface of C.P.Ti by glow plasma surface metallurgy process and its corrosion resistance was elevated by electrochemical testing method. The results indicate that the Ti-Pd alloying coating has better crevice corrosion resistance than Ti-0.2Pd in NaCl and HCl saturated water solution at 100 ℃ and in 8.6%H2SO4 water solution at 40 ℃. The corrosion rate of Ti-Pd alloying coating is only 0.682 mm/a in 80%H2SO4 water solution and 0.004 mm/a in 30%HCl water solution at room temperature. And it is only 18.2% and 12.5% of Ti-0.2Pd alloy corrosion rate under the same condition respectively.