(001) textured CoPt-Ag nanocomposite films for high-density perpendicular magnetic recording

S.X. Xue,H. Wang,H.B. Wang,F.J. Yang,J.A. Wang,X. Cao,Y. Gao,Z.B. Huang,Z.Y. Li,Q. Li,S.P. Wong

DOI: https://doi.org/10.1016/j.jmmm.2006.02.252

IF: 3.097

2006-01-01

Journal of Magnetism and Magnetic Materials

Abstract:CoPt/Ag nanocomposite films were prepared by magnetron sputtering. The dependence of texture and magnetic properties on film thickness, Ag atomic fraction and annealing conditions is investigated. Films with a thickness about 20nm are easy to form with (001) orientation. The existence of the Ag in the film plays a dominant role in inducing the (001) texture of the film and suppressing the growth of the CoPt grains during annealing. The Co35Pt38Ag27 film after annealing at 600°C exhibits a large perpendicular coercivity of 5.6kOe and a squareness of 0.90 with a small average grains size of 12.5nm.