Preparation, characterization and drug release property of paclitaxel nanoparticles
Zhan-jun Liu,Wei-guo Zhang,Jiu-gao Yu,Gang Han,Hong-guang Dai
2009-01-01
Abstract:Background: Paclitaxel is a natural anticancer drug, which has demonstrated significant activity in clinical trials. However, it has been limited due to poor aqueous solubility. Chitosan can be modified into graft copolymer, which changed into nanoparticles in aqueous solution, and employed as controlled release carriers for drugs. Objective: To study the characterization, in addition, to evaluate in vitro drug release ability of paclitaxel nanoparticles. Design, time and setting: A repeated measurement design was conducted at the Laboratory of North China Coal Medical University from January 2008 to July 2008. Materials: The average molecular weight of 2.0 × 10 5 chitosan with 92% deacetylation degree was produced by Golden-shell Biochemical Co., Ltd. Paclitaxel (lot number: 082329802) was provided by National Institute for the Control of Pharmaceutical and Biological Products. Methods: The potassium diperiodaton-ickelate served as initiator, chitosan-graft-vinyl acetate copolymers were synthesized by free radical graft copolymerization, which could be directly transformed into nanoparticles with hydrophobic core and hydrophilic surface in the water medium. Paclitaxel nanopartioles were prepared via mixture 0.5-5.0 mg paclitaxel with nanoparticles by ultrasonic irradiation technology. Main outcome measures: Particles size, polydispersity index zeta potential was detected by laser particle size analyzer. The morphology of chitosan nanoparticles and paclitaxel nanoparticles was observed by transmission electron microscope. In addition, encapsulation capability, loading content and in vitro drug release of the paclitaxel nanoparticles was analyzed by high-performance liquid chromatography. Results: The mean diameters of chitosan nanoparticles and paclitaxel nanoparticles were 196.2 nm and 320.8 nm, respectively. The nanoparticles possessed a uniform particles size distribution and an obvious positive charge surface, but the Zeta potential had no significant difference (F=0.818, F=3.38, all P > 0.05). The dose of paclitaxel could affect the encapsulation rate, which could up to 93.6% when added the quantity of paclitaxel was 2% of anoparticles. The results of simulate drug release showed that drug release was reach 48.3% in 24 hours at the burst release phase, which up to 75.9% at 175 hours longer in the slower release phase. The encapsulation rate of drug-loaded nanoparticles was stable. Conclusion: The preparation method is reliable and simple. The nanoparticles possessed good physical performance and sustained release character in vitro.