Abstract:VO2 nanobelts with metal–semiconductor properties were prepared through low temperature hydrothermal reaction and post annealing. X-Ray diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), differential scanning calorimetry (DSC) and UV-vis-NIR spectrophotometry were employed to investigate the evolution of structure, morphology and properties of the VO2 nanobelts. The results illustrate that the pure VO2 (B) nanobelts can be obtained by hydrothermal reaction. The shape of the nanobelts evolves with hydrothermal temperature, time and reactant concentration. With the increasing of hydrothermal temperature from 160 °C to 200 °C, the nanobelts become homogenous and regular. The regular nanobelts are also obtained by the decrease of V2O5 concentration. Samples prepared at 200 °C over 48 h have superior morphology and crystallinity. After annealing, VO2 (B) can be transformed into VO2 (M), which is dependent on the hydrothermal conditions. Samples prepared at 160 °C over 48 h and 180 °C over 48 h can be transformed into VO2 (M) at 450 °C over 2 h, while samples obtained at 200 °C over 48 h should be annealed at 500 °C for 2 h. The nanobelts are transformed into irregular nanostructures, nanorods and nanobelts at the hydrothermal temperatures of 160 °C, 180 °C and 200 °C, respectively. However, samples prepared at 200 °C over 48 h with a V2O5 concentration of 0.0125 M can keep the intact nanobelts after annealing. The DSC analysis proves that the VO2 (M) shows good phase transition behavior around 68 °C and the phase transition temperature can be reduced to 58 °C by 0.5 at% tungsten doping. After mixing the VO2 (M) with acrylic resin, the visible transmission of the VO2 composite coating on glass is up to 52.2% and the solar modulation at 2000 nm is up to 31.5%, which means that it is a good candidate for smart windows.

Synthesis and field emission property of VO2 nanorods with a body-centered-cubic structure

Synthesis and optical properties of nanorods

Facile synthesis of Zn 1−x Cu x O nanorods with a very broad visible band

Synthesis And Optical Properties Of V2o5 Nanorods

Controlled synthesis of VO2(R), VO2(B), and V2O3 vanadium-oxide nanowires

Self-Assembly and Horizontal Orientation Growth of Vo2 Nanowires

Ultra-Long, Free-Standing, Single-Crystalline Vanadium Dioxide Micro/Nanowires Grown by Simple Thermal Evaporation

Synthesis, optical and field electron emission properties of low-dimensional ZnO nano-structures

Synthesis and Electrochemical Characterization of 3D VO2(B) Nanostructures

Synthesis and magnetic properties of CeVO3 nanostructures

Preparation of Single-Crystalline NdVO4 Nanorods, and Their Emissions in the Ultraviolet and Blue under Ultraviolet Excitation

Preparation of VO2 nanowires and their electric characterization

Structural, Photoluminescence, and Field Emission Properties of Vertically Well-Aligned Zno Nanorod Arrays

Photoluminescence and Field Emission of 1D ZnO Nanorods Fabricated by Thermal Evaporation

Synthesis of LiV 3 O 8 nanorods and shape-dependent electrochemical performance

Vanadium Pentoxide Nanobelts and Nanorolls: from Controllable Synthesis to Investigation of Their Electrochemical Properties and Photocatalytic Activities

Rapid, low-temperature synthesis of single-crystalline Co3O 4 nanorods on silicon substrates on a large scale

Synthesis and Phase Transition Behavior of Undoped VO2 with a Strong Nano-Size Effect

Oxygen deficient V2O5 nanorods for gas sensing

Study of nanocrystalline VO2 thin films prepared by magnetron sputtering and post-oxidation

A Facile Process to Prepare One Dimension VO2nanostructures with Superior Metal–semiconductor Transition