Microwave absorption properties of composite fine powder synthesized by polycarbonsilane precursor/magnetic powder

Renchao Che,Yongqing Li,Zhaohui Chen,Hongji Lin

DOI: https://doi.org/10.1023/A:1006662007226

1999-01-01

Journal of Materials Science Letters

Abstract:With the improvement of the high technology industry, intensive research is devoted to composite materials to obtain properties that cannot be achieved by any of the elemental parts acting alone [1]. There are more and more requirements for the preparation technology of microwave absorption material. The production of composite fine powder whose electromagnetic property in microwave-band can be easily changed has an important significance on the national defense industry. Fine composite powder has special physical, chemical and magnetic properties [2]. Various synthetic methods have been developed to prepare composite fine powder. In this study, a new processing routine which is composed of the chemical disproportion method and heat treatment is used to prepare fine composite powder. The fine magnetic powder was synthesized by a chemical precipitation routine. The powder was washed in acetone and mixed with polycarbonsilane. The mixture was subjected to heat treatment at different temperatures. Lastly, the samples were studied by XRD and thermal gravimetric (TG) analysis. The radar absorption properties of the fine composite powder were tested in X band (8.2‐12.4 GHz). The XRD analysis results show that fine magnetic powder deposited from the reaction solution was amorphous material. They were crystallized after heat treatment. Fine composite powder consists of Fe3Si, Co3C and a little SiC. The greater the amount of polycarbonsilane in the mixture, the more the amount of the metal composition in the powder. The powder particle size is 50‐200 nm. The TG analysis results are showed in Figs 1 and 2. From the TG analysis results, we can conclude that during the heat treatment process the weight of the sample, into which was added some PCS, was reduced to 70% of its origin level. The reason is that the polycarbonsilane was disintegrated into free carbon and amorphous SiC at certain temperature, subsequently giving out gases which were mainly composed of CO and CH4. Subsequently, added PCS can decrease the weight of the samples. A reduction of the microwave absorption material’s weight is beneficial to its applicance. In addition, adding polycarbonsilane (PCS) can change the thermal behavior of the samples. In the range of 700‐800 ‐ C, the crystallographic structure of composite fine powder is stable.