Abstract:We designed and synthesized new indolocarbazole-triazine derivatives, 9-di-tert-butyl-5,7-bis(4-(4,6-diphenyl-1,3,5-triazin-2-yl)phenyl)-5,7-dihydroindolo[2,3-b]carbazole (2TRZ-P-ICz) and 3,9-di-tert-butyl-5,7-bis(5'-(4,6-diphenyl-1,3,5-triazin-2-yl)-[1,1':3',1″-terphenyl]-2'-yl)-5,7-dihydroindolo[2,3-b]carbazole (2TRZ-TP-ICz), as new bipolar host materials for red phosphorescent OLEDs. In the film state, 2TRZ-P-ICz and 2TRZ-TP-ICz exhibited photoluminescence maxima at 480 nm and 488 nm, respectively. The dipole moment characteristics of the new compounds under various solvent conditions were investigated using the Lippert-Mataga equation. The results showed that the dipole moment of 2TRZ-P-ICz is 26.9D, while that of 2TRZ-TP-ICz is 21.3D. The delayed fluorescence lifetimes were 0.188 μs for 2TRZ-P-ICz and 2.080 μs for 2TRZ-TP-ICz, with 2TRZ-TP-ICz showing TADF characteristics. Additionally, 2TRZ-TP-ICz was found to have a ΔEST of less than 0.2 eV. The triplet energy levels of the newly synthesized bipolar host materials were found to be 2.72 and 2.75 eV, confirming their suitability for use in red phosphorescent OLEDs. To investigate the carrier mobility of the synthesized materials, hole-only devices and electron-only devices were fabricated and tested. The hole mobility value at 1V was found to be 3.43 × 10-3 cm2/Vs for 2TRZ-P-ICz and 2.16 × 10-3 cm2/Vs for 2TRZ-TP-ICz. For electron mobility at 1V, 2TRZ-P-ICz showed a value of 4.41 × 10-9 cm2/Vs, while 2TRZ-TP-ICz exhibited a value of 9.13 × 10-9 cm2/Vs. As a result, when the new material was used as a host in red phosphorescent OLEDs, 2TRZ-TP-ICz achieved a current efficiency of 9.92 cd/A, an external quantum efficiency of 13.7%, CIE coordinates of (0.679, 0.319), and an electroluminescence maximum wavelength of 626 nm.

The host materials containing carbazole and oxadiazole fragment for red triplet emitter in organic light-emitting diodes

Distinct phosphorescence enhancement of red-emitting iridium(III) complexes with formyl-functionalized phenylpyridine ligands

Perceiving the influence of phenyl-carbazole isomers on sulfone/thioxanthone-based D–A–D hosts: realizing efficient red-phosphorescent OLEDs

Pure Red Iridium(III) Complexes Possessing Good Electron Mobility with 1,5-Naphthyridin-4-ol Derivatives for High-Performance OLEDs with an EQE over 31.

Novel bipolar host materials including carbazole and dioxy[2,3-b] pyrazine units for red phosphorescent organic light-emitting diodes

Carbazole-pyridine pyrroloquinoxaline/benzothiadiazine 1,1-dioxide based bipolar hosts for efficient red PhOLEDs

Efficient, saturated red electroluminescent devices with modified pyran-containing emitters

Carbazole/Benzimidazole-Based Bipolar Molecules as the Hosts for Phosphorescent and Thermally Activated Delayed Fluorescence Emitters for Efficient OLEDs

Two novel bipolar hosts based on 1,2,4-triazole derivatives for highly efficient red phosphorescent OLEDs showing a small efficiency roll-off

Highly efficient red and green phosphorescent OLEDs based on benzonitrile and carbazole as bipolar host materials

9-(9-Alkylcarbazol-3-yl)-3-(methoxypyridin-3-yl)carbazoles as host materials for very efficient OLEDs

New Bipolar Host Materials Based on Indolocarbazole for Red Phosphorescent OLEDs

N-Aryl carbazole derivatives for non-doped red OLEDs

New bipolar host materials based on isoquinoline and phenylcarbazole for red PhOLEDs

Carbazolylphosphines and carbazolylphosphine oxides: facilely synthesized host materials with tunable mobilities and high triplet energy levels for blue phosphorescent OLEDs

Novel benzothiadiazine 1,1-dioxide based bipolar host materials for efficient red phosphorescent organic light emitting diodes

Red emissive organic light-emitting diodes based on codeposited inexpensive CuI complexes

Exciplex-forming Co-host Systems Featuring Highly Twisted Bis-(N-carbazolyl)benzene-based Donors for High Efficiency Orange OLEDs

Orange and red emitting OLEDs based on phenothiazine polymers

Carbazole‐Based Iridium(III) Complexes for Electrophosphorescence with EQE of 32.2% and Low Efficiency Roll‐Off

Alkyl-Substituted Carbazole/Pyridine Hybrid Host Materials for Efficient Solution-Processable Blue- and Green-Emitting Phosphorescent OLEDs