Abstract:In this paper, X‐ray–induced multicolor long afterglow and photostimulated luminescence from Sr3(PO4)2: Pr3+ was reported. The Rietveld refinement results have confirmed the as‐prepared sample was pure Sr3(PO4)2 phase with hexagonal crystal system. And Sr3(PO4)2: Pr3+ showed an excellent X‐ray–induced long afterglow luminescent performance. Under the excitation of X‐ray, the sample showed multicolor long afterglow luminescence from UVC to red region located at 268, 359, 466, 548, 604.3 and 685 nm, which can be ascribed to 4f5d‐3H4, 4f5d‐ 1D2, 4f5d‐3P0, 3P0→3H5 and 1D2→3H4, respectively. And the strongest afterglow emission intensity appeared at 468 nm. Furthermore, only 30 s X‐ray irradiation can induce 12 h afterglow emission, which afterglow emission intensity of 468 nm still reached 3.71 × 104 cps and was about 37.1 times stronger than the background intensity. In particular, the relation between 268 nm afterglow emission intensity and 468 nm afterglow emission intensity showed good linearity. And the UVC afterglow emission can be easily "observed" via the visible afterglow light. Furthermore, Sr3(PO4)2: Pr3+ possessed an excellent photostimulated luminescence (PSL) under the excitation of 980 nm NIR laser and the PSL intensity of the 12 circle still arrived at 1.26 × 105 cps, which was about 37.1 times stronger than the afterglow emission intensity after 5 h decay. All these results showed that the as‐prepared Sr3(PO4)2: Pr3+ phosphor was an excellent X‐ray–induced long afterglow luminescence phosphor, which possessed large potential applications in the medical field.

Luminescence Properties of Sm3+-doped Sr3Sn2O7 Phosphor

The Synthesis and Afterglow Luminescence Properties of A Novel Red Afterglow Phosphor: Zro2:Sm3+,Sn4+

Synthesis and Luminescence Properties of a Novel Red SrMoO4:Sm3+,R+ Phosphor

The Photoluminescence and Afterglow Properties of Ca 2 SnO 4 :Sm 3+ Phosphor

Crystal structure and luminescence properties of thermally stable Sm3+-doped Sr9In(PO4)7 orange-red phosphor

Photoluminescence and afterglow behavior of orange-reddish Pr3+-activated Sr3Al2O6 phosphor

X‐ray–induced multicolor long afterglow and photostimulated luminescence from Pr3+‐doped Sr3(PO4)2

Preperation and Photoluminescent Properties of Ca2AlSi3O2N5:Sm3+ Phosphor

Photoluminescence characteristics of Sm3+ doped Na13Sr2Ta2(PO4)9 as new orange-red emitting phosphors

Red-Emitting SrGa 2 O 4 :Cu 2+ Phosphor with Super-Long Persistent Luminescence

Ultraviolet and visible persistent luminescence from Sr3MgSi2O8:Pr3+

Photoluminescence of Sr2p2o7:Sm3+ Phosphor As Reddish Orange Emission for White Light-Emitting Diodes

Persistent Luminescence in Rare Earth Ion-Doped Gadolinium Oxysulfide Phosphors

Effect of Sm3+ co-doping on the luminescence behavior of Pr3+-activated Sr3Al2O6 orange-reddish phosphors

Luminescent properties of long afterglow MAl2Si2O8:Eu2+, Dy2+ (M=Ca, Sr, Ba) photoluminescent materials

Luminescence properties and energy transfer of a red-emitting Ca3 (PO4)2:Sm3+, Eu3+ phosphor

Photoluminescence, cathodoluminescence and thermal stability of Sm3+ -activated Sr3 La(VO4 )3 red-emitting phosphors

Luminescence Properties and Optical Sensing Behaviors of Sr2GdSbO6:Eu3+ Phosphors

Multifunctional Near-Infrared Luminescence Performance of Nd3+ Doped SrSnO3 Phosphor

Preparation and Luminescence Properties of Orange-Red Ba 3 Y 4 O 9 :Sm 3+ Phosphors

Luminescence enhancement and energy transfers of Ce3+ and Sm3+ in CaSrSiO4 phosphor