Preparation and Tribological Behavior of Compositionally Graded ZrN Coatings

奚运涛,刘道新,韩栋

DOI: https://doi.org/10.3969/j.issn.1007-9289.2009.03.005

2009-01-01

China surface engineering

Abstract:Four kinds of different compositionally graded ZrN coatings were prepared on 2Cr13 stainless steel by ion plating. The element distribution on the layer depth was analyzed by glow discharge spectrometer (GDS). The supporting capacities under static load conditions of these coatings were evaluated using a micro-hardness tester. The tribological behaviors of compositionally graded ZrN coatings were investigated on the basis of a ball-disk wear tester. The results show that the coating/substrate bonding strength and the supporting capacity of coatings will be reduced if its compositionally graded is too small. However, the ductility and the resistance of the fatigue property of coatings will be deceased if it is no compositionally graded. When the compositionally graded of coatings is 3~8 layers and the thickness of every layer is more than 0.5 μm, the tribological property of ZrN coatings will be improved obviously because it will reduce the discontinuity of stresses between the coating and substrate and increase the ductility, the coating/substrate bonding strength and the supporting capacity.