Abstract:A facile method to prepare monodisperse polystyrene (PS)/cross-linked PS particles was studied by combining hydrothermal process with dispersion polymerisation. Compared to traditional dispersion polymerisation, in this way the polymerisation of styrene in ethanol-water media could be carried out in a relatively wide ethanol/water ratio range from 10/90 to 70/30, consequently monodisperse particles from 160 to 1300 nm in size were generated at 80 degrees C. It implies that the monodisperse PS particles could be acquired simply and the significant change in PS particle size could be adjusted by only varying the ethanol/water ratio. The phenomenon could be inferred that the hydrothermal process improved the solubility of the monomer in the media under a higher reaction pressure, which enabled this method to expand the ethanol/water ratio range for traditional dispersion polymerisation. Furthermore, the monodisperse cross-linked PS particles could also be obtained even at the cross-linking agent being up to 2% without addition of stabiliser through this method. Not using stabiliser could enlarge the application range of the cross-linked monodisperse PS particles. The formation process of the particles was detected using scanning electron microscopy. The particle morphology transformation along with hydrothermal reaction in the early stage was demonstrated, that is, the initial irregular particles in different size congregated gradually to form monodisperse particles.

Preparing of monodisperse and cation-charged polystyrene particles stabilized with polymerizable quarternary ammonium by dispersion polymerization in a methanol-water medium.

Preparation of monodisperse polystyrene particles and assembly of spherical colloidal crystals

Micron-Size Functional Uniform Pmma Particles by Dispersion Copolymerization in Polar Media

Micron-Size Uniform Poly(Methyl Methacrylate) Particles by Dispersion Polymerization in Polar Media 1. Particle Size and Particle Size Distribution

Preparation of Monodisperse and Anion‐Charged Polystyrene Microspheres Stabilized with Polymerizable Sodium Styrene Sulfonate by Dispersion Polymerization

Synthesis and Characterization of Amphiphilic Centipede-Like Copolymer PS-PS-PMAA

Controllable Preparation of Monodisperse Polystyrene Microspheres with Different Sizes by Dispersion Polymerization

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Facile Method to Prepare Monodisperse Polystyrene Particles by Hydrothermal Process

Preparation of Monodisperse Polystyrene Spheres in Aqueous Alcohol System

A Novel Method for Preparing Monodispersed Polystyrene Nanoparticles

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

PREPARATION OF MONODISPERSE CROSS-LINKED POLYSTYRENE MICROSPHERES BY COMBINING DISPERSION POLYMERIZATION WITH HYDROTHERMAL PROCESS

Preparation and Characterization of Poly(methyl methacrylate) Particles by Combined Dispersion and Emulsion Polymerization

Nonaqueous Dispersion Polymerization of Styrene in Methanol with the Ionomer Block Copolymer Poly[(4-Methylstyrene)-Co-(4-Vinyltriethylbenzyl Ammonium Bromide)]-B-Polyisobutene As A Stabilizer

Styrene mini-emulsion polymerization co-stabilized by predissolved fluoropolymer

Preparation of micron-size crosslinked microspheres by dispersion copolymerization of polystyrene/2,2′-oxy-bisethanol diacrylate

PARTICLE FEATURES AND FORMATION MECHANISM OF POLYSTYRENE-POLY(METHYL METHACRYLATE) COMPOSITE PARTICLES PREPARED BY SUSPENSION-EMULSION COMBINED POLYMERIZATION

Preparation of Styrene–Maleic Anhydride Random Copolymer by Stabilizer-Free Dispersion Polymerization

Dispersion Copolymerization of Styrene and Glycidyl Methacrylate in Polar Solvents