The valence electron structure and the properties of (ZrTi)B2 solid-solution

Jiecai Han,Jinping Li,Songhe Meng,Xinghong Zhang,Xiaoguang Luo

DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.z2.004

2007-01-01

Rare Metal Materials and Engineering

Abstract:The two kind of Ti-rich (Ti0.8Zr0.2)B-2 and Zr-rich (Zr0.8Ti0.2)B-2 permutation solid-solutions were formed by hot pressing. To forecast the properties of the two solid-solutions, their valence electron structure was analyzed on the base of the empirical electron theory (EET) of solids and molecules, and compared with that of the TiB2 or ZrB2 matrix. The results showed that, after the TiB2-dissolved into the ZrB2 matrix, the step number of Zr decreased from Al6 to A14, the parameters of the valence electron structure decreased, which indicated that the TiB2 dissolution resulted in the decrease of hardness, strength and melting point and in the rise of the toughness of the ZrB2 matrix. While after ZrB2 dissolved into the TiB2 matrix, the step number of Ti increased form A13 to A15. So it is concluded the effect of the ZrB2 dissolution was opposite to that of the TiB2 dissolution. Because the parameters of the four phases were almost isometric, the interface solid-solution reaction of the TiB2 and ZrB2 took place easily and the TiB2 and ZrB2 dissolving mutually has changed the properties of the matrixes slightly when hot pressed.