Abstract:International Journal of Modern Physics B, Ahead of Print. This paper describes a simple approach for creating silver (Ag) nanocubes using pulsed laser ablation in a liquid medium. The development of nanocubical formations of Ag obtained by laser ablation using Nd: YAG laser was conducted for 5, 10, 15, and 20[math]min. The surface morphological analysis was performed using field-emission scanning electron microscopy (FESEM) to show the formation of silver nanocubes with edge lengths ranging from 150[math]nm to 250[math]nm. The UV-visible spectroscopy demonstrates that the concentration of Ag nanostructures, evidenced by the characteristic localized surface plasmon resonance band near 400[math]nm in the colloidal solution containing Ag nanoparticles, increased with the increasing laser ablation duration from 5[math]min to 20[math]min. The growth mechanism for Ag nanocubes can be easily understood with the change in laser ablation time from 5 to 10, 15, and then 20[math]min. The Ag sheets with no specific shape start to develop after 5 min of laser ablation, and after 10[math]min, larger particles form. Then, after 15[math]min, a small number of cube-like nanostructures with rough and uneven edges was obtained. At the end of 20[math]min, a complete cubic formed with fine and distinct edges and a very large amount of nanocubes. The elemental silver signal was present in Ag nanocubes, as revealed by the energy-dispersive X-ray spectroscopy (EDS) spectra. The produced Ag nanocubes may be used to construct two-dimensional nanocomposites with practical applications in the electrical, optoelectronic, electrochemical, and biological areas.

Synthesis of Perfect Silver Nanocubes by a Simple Polyol Process

Seed-mediated synthesis of silver nanocrystals with controlled sizes and shapes in droplet microreactors separated by air.

Robust, Reproducible, and Scalable Synthesis of Silver Nanocubes

Synthesis of Silver Nanocubes and Factors Affecting the Size and Shape of Sliver Nanoporticles

Seed-Mediated Synthesis Of Ag Nanocubes With Controllable Edge Lengths In The Range Of 30-200 Nm And Comparison Of Their Optical Properties

Morphology and Composition Controlled Synthesis of Flower-Like Silver Nanostructures.

Robust Synthesis of Silver Nanocubes in Oil Phase

Toward the Synthesis of Sub-15 nm Ag Nanocubes with Sharp Corners and Edges: The Roles of Heterogeneous Nucleation and Surface Capping

Synthesis and Characterizing of High Aspect Ratio Silver Nanowires by Polyol Process

A Simple Method for Preparation of Silver Dendrites

Study On The Synthesis Of Silver Nanowires With Adjustable Diameters Through The Polyol Process

Effect of light at different wavelengths on polyol synthesis of silver nanocubes

Synthesis and Characterization of Silver Nanoparticles Using Simple Polyol Method

Preparation and Microstructure of Silver Nanopowder with Spheric Morphology

Development of silver nanocubes created by pulsed laser ablation in liquid

Recent Developments In Shape-Controlled Synthesis Of Silver Nanocrystals

Mesoporous Ag Nanocubes Synthesized Via Selectively Oxidative Etching at Room Temperature for Surface-Enhanced Raman Spectroscopy

Silver Nanocubes: From Serendipity to Mechanistic Understanding, Rational Synthesis, and Niche Applications

A Simple and Effective Route for the Synthesis of Crystalline Silver Nanorods and Nanowires

Synthesis, characterization and self-assembly of silver nanowires

Synthesis and Analysis of Polymorphic Silver Nanoparticles and Their Incorporation into the Polymer Matrix