Abstract:A new family of alternate poly(ester-anhydrides) containing aliphatic and aromatic diacids were synthesized. The dicarboxylic acids were obtained by derivatization of p-hydroxy benzoic acid at the hydroxy terminus with cyclic anhydride (adipic anhydride and succinic anhydride) and subsequently polymerized via the corresponding mixed anhydrides by melt polycondensation. DSC traces revealed that the polymers had low Tg (<40°C) and no crystallinity. The static contact angle measurements indicated that the poly(ester-anhydrides) were more hydrophobic than poly(d,l-lactide) and poly(adipic anhydride). In vitro degradation of the polymers was also investigated in pH 7.4 PBS at 37°C. It was found that degradation rate of the poly(ester-anhydrides) increased with p-carboxy phenyl adipic monoester (CPA) content in the polymers and the degradation duration could be adjusted from ca. 20 days to ca. 2 months. Erosion curve of poly(p-carboxy phenyl adipic monoester anhydride) (PCPA) was characterized by a linear region of weight loss at nearly constant rate in the first 7 days (ca. 80% of weight loss) followed by a gradual decrease region. IR and SEM analysis showed that significant erosion of PCPA occurred in the outer layer and no apparent erosion could be seen in the inner layer of the degrading sample after 7-day degradation. The poly(ester-anhydrides) may be used as either anti-infective polymeric prodrugs or matrices for drug delivery.

Synthesis and Characterization of Novel Biodegradable Aromatic–aliphatic Poly(ester Amide)s Containing Ethylene Oxide Moieties

Synthesis and Characterization of New Unsaturated Degradable Poly(Ether Ester Amide)S Containing Ethylene Oxide Moieties

Synthesis, characterization and in vitro degradation of a new family of alternate poly(ester-anhydrides) based on aliphatic and aromatic diacids

Synthesis, Characterization, and Thermal Properties of Biodegradable Polyetheresteramide Copolymers Based on 11-Aminoundecanoic Acid

Synthesis and Characterization of Novel Biodegradable Polyamides Containingα-amino Acid

Synthesis and Characterization of Novel Biodegradable Poly(Ester Amide) with Ether Linkage in the Backbone Chain

Synthesis, characterization and properties of poly(aryl ether amides) containing methoxy substituted phthalazinone moiety

Synthesis and Characterization of Amino Acid Derived Biodegradable P (Ester-Amide )

Synthesis And Characterization Of Poly(Ether Amide)S Containing Bisphthalazinone And Ether Linkages

Design,preparation and Characterization of Biodegradable Poly(ester-Amide)

One‐pot Synthesis of Biodegradable and Linear Poly(ester Amide)s Based on Renewable Resources

Synthesis and characterization of biodegradable alternating polyesteramides from mixed diamidediols and sebacic acid

Synthesis, Characterization, and Properties of Novel Polyetherester Polyols and Developed Polyurethanes

One-Pot Synthesis and Characterization of Hyperbranched Poly(Ester-Amide)S from Commercially Available Dicarboxylic Acids and Multihydroxyl Secondary Amines

Synthesis and characterization of new poly(ether amide)s based on a new cardo monomer

Synthesis and Specific Biodegradation of Novel Polyesteramides Containing Amino Acid Residues

Synthesis of New Aromatic Poly(Amide Imide)S from Unsymmetrical Extended Diamine Containing A Phthalazinone Moiety

Synthesis,Characterization and Degradation of Poly(Ester-Amide) Derived from L-Lactic Acid and α-Phenylalanine

Synthesis and Characterization of Poly(ether Amide)s Containing Biphenylphthalazinone Moiety

Synthesis of New Soluble Aromatic Poly(Amide Imide)S from Unsymmetrical Extended Diamine Containing Phthalazinone Moiety

Synthesis and Characterization of Aliphatic Poly(Ester-Amide)S Containing Symmetrical Bisamide Blocks