Comparative Study of Electrical Transport of(1-x)La_(0.67)Ca_(0.33)MnO_3/xCuO and La_(0.67)Ca_(0.33)Mn_(1-x)Cu_xO_3

Miao Juhong,Yuan Songliu,Yin Shiyan

DOI: https://doi.org/10.3321/j.issn:1000-4343.2009.06.012

2009-01-01

Abstract:The samples with nominal composition of(1-x)La0.67Ca0.33MnO3/xCuO(LCMO/CuO)and La0.67Ca0.33Mn1-xCuxO3(LCMCO)were fabricated using different methods.The Cu content level(x) dependence on electrical transport behavior was investigated under a wide temperature range.It was found that the two series of samples had different behavior.For LCMCO,the metal-insulator transition temperature(Tp) decreased sharply with increment of x and exhibited insulator behavior when x=5.5%.While for LCMO/CuO composites,Tp shifted towards low temperature with the increase of x when x≤6%,and the samples exhibited similar electrical transport behavior when x≥6%.Furthermore,the low-field magnetoresistance(LFMR) was enhanced in both samples.The MR0 values at a magnetic field of 0.3 T for the two samples could reach ~76% and ~88%,respectively.Based on the analysis of microstructure and sample preparation process,it was discussed that the enhancement of LFMR was attributed to the formation of Cu dependent materials with local spin disorder at grain boundaries.