Abstract:The corrosion phenomenon and its economic impacts can hardly be ignored in any application. This study synthesized a quaternary ammonium salt (3) containing hydrophobic dodecyl and electron-rich diallylbenzyl amine moieties to be used in 15 % HCl as a corrosion inhibitor of mild steel. Several techniques, such as 1H and 13C NMR, IR, TGA, and elemental analysis, have been used to characterize inhibitor 3. Popular corrosion measurement techniques, namely weight loss, potentiodynamic polarization techniques, and electrochemical impedance spectroscopy, have been used to determine the efficiency of inhibitor 3. At 303 K and a moderately low concentration of 50 ppm, the quaternary ammonium salt-based inhibitor demonstrated a maximum efficiency of ≈95.0 %. At elevated temperatures of 313, 323, and 333 K, the inhibition efficacy values were recorded as 91.3, 82.8, and 75.0 %, respectively. Adsorption isotherm study revealed that the adsorption of inhibitor 3 followed Langmuir adsorption isotherm. The value of Δ G a d s ° was found to be - 40.19 kJ mol-1, indicating that inhibitor 3 became adsorbed via a mixed physi-chemisorption mechanism. A very high adsorption constant ( K a d s ) of 1.53 × 105 L mol-1 suggested strong adsorption of inhibitor 3. The difference in activation energy ( E a ) value of 42.4 kJ mol-1 between the control and the inhibited solution indicated an efficient adsorption of inhibitor 3. The ability of inhibitor 3 to retard both anodic and cathodic half-cell reactions was proved via open circuit potential and Tafel curves studies. Detailed discussions on the change in corrosion current densities ( i c o r r ), polarization ( R p ) and charge transfer ( R c t ) resistances have been offered to discuss the inhibition efficiency. Water contact angle measurement showed a drastic increase in mild steel surface hydrophobicity following inhibitor 3 adsorption. SEM-EDX and XPS studies confirmed the definitive presence of inhibitor 3 on the mild steel surface. Density functional theory (DFT) studies revealed the frontier molecular orbitals with which the metal surface interacts. A detailed corrosion inhibition mechanism has been offered in the context of adsorption isotherm and DFT studies.

The adsorption and corrosion inhibition of some cationic gemini surfactants on carbon steel surface in hydrochloric acid

Some New Synthesized Gemini Cationic Surfactants as Corrosion Inhibitors for Carbon Steel in Hydrochloric Acid Solution

Experimental and Theoretical Investigation of 1-Hexyl-3-methylimidazolium Iodide As a Corrosion Inhibitor for Mild Steel in HCl Environment

Imidazoline Gemini Surfactants as Corrosion Inhibitors for Carbon Steel X70 in NaCl Solution

Gemini cationic surfactant of 1, 3-bis (dodecyl dimethyl ammonium chloride) propane as a novel excellent inhibitor for the corrosion of cold rolled steel in HCl solution

Synthesis, surface activity, and corrosion inhibition capabilities of new non-ionic gemini surfactants

Influence of Hydroxyl Groups on the Inhibitive Corrosion of Gemini Surfactant for Carbon Steel

Synthesis and Characterization of a Novel Nonionic Gemini Surfactant as Corrosion Inhibitor for Carbon Steel in Acidic Solution

Synthesis, Anti-corrosion Performance and Mechanism Research of Amphoteric Gemini Surfactant(TCDSQ-22) as Corrosion Inhibitor on Stainless Steel

An electrochemical, and surface studies of synthesized Gemini ionic liquid as corrosion inhibitor for carbon steel in petroleum field

Effect of anion on the corrosion inhibition of cationic surfactants and a mechanism study

The inhibition performance of heterocyclic compounds on Q235 steel in methanol/formic acid medium: Experimental and theory

An Eco-Friendly Quaternary Ammonium Salt as a Corrosion Inhibitor for Carbon Steel in 5 M HCl Solution: Theoretical and Experimental Investigation

Synthesis of Gemini-type imidazoline quaternary ammonium salt using by-product fatty acid as corrosion inhibitor for Q235 steel

Impacts of pyridinium gemini surfactants on corrosion inhibition of carbon steel

Experimental and theoretical investigations on synergistic effect of surfactants as corrosion inhibitor on steel in acid medium

CORROSION INHIBITION EFFECT OF BISQUATERNARY AMMONIUM SALT OF ROSIN GROUP TO MILD STEEL IN HYDROCHLORIC ACID

Synthesis, characterization, and corrosion protection potential of a highly effective and water‐miscible surfactant for mild steel in sulfuric acid solution

pH‐responsive chitosan microspheres loaded with Gemini imidazolium‐based ionic liquids as smart corrosion inhibitors for N80 steel in hydrochloric acid solution

Some New Nonionic Surfactants Based on Propane Tricarboxylic Acid as Corrosion Inhibitors for Low Carbon Steel in Hydrochloric Acid Solutions

Synthesis of a new quaternary ammonium salt for efficient inhibition of mild steel corrosion in 15 % HCl: Experimental and theoretical studies