Abstract:The various wastes generated by silkworm silk textiles that are no longer in use are increasing, which is causing considerable waste and contamination. This issue has attracted widespread attention in countries that use a lot of silk. Therefore, enhancing the mechanical properties of regenerated silk fibroin (RSF) and enriching the function of silk are important directions to expand the comprehensive utilization of silk products. In this paper, the preparation of RSF/Al2O3 nanoparticles (NPs) hybrid fiber with different Al2O3 NPs contents by wet spinning and its novel performance are reported. It was found that the RSF/Al2O3 NPs hybrid fiber was a multifunctional fiber material with thermal insulation and UV resistance. Natural light tests showed that the temperature rise rate of RSF/Al2O3 NPs hybrid fibers was slower than that of RSF fibers, and the average temperature rose from 29.1 °C to about 35.4 °C in 15 min, while RSF fibers could rise to about 40.1 °C. UV absorption tests showed that the hybrid fiber was resistant to UV radiation. Furthermore, the addition of Al2O3 NPs may improve the mechanical properties of the hybrid fibers. This was because the blending of Al2O3 NPs promoted the self-assembly of β-sheets in the RSF reaction mixture in a dose-dependent manner, which was manifested as the RSF/Al2O3 NPs hybrid fibers had more β-sheets, crystallinity, and a smaller crystal size. In addition, RSF/Al2O3 NPs hybrid fibers had good biocompatibility and durability in micro-alkaline sweat environments. The above performance makes the RSF/Al2O3 NPs hybrid fibers promising candidates for application in heat-insulating and UV-resistant fabrics as well as military clothing.

Preparation and Property Characterization of Regenerated Tussah Silk Fibroin Power by Urea Solvent System

Modification on the Chemi-mechanical Pulping Property of Rice Straw with Alkali-urea System

Fabrication and characterization of porous tubular silk fibroin scaffolds.

Study on Emulsification of Silk Fibroin Solution

Absorption Properties of Silk Fibroin/Acrylic Acid/Acrylamide Composite Absorbent Material

Advances in Preparation and Properties of Regenerated Silk Fibroin

EDC/NHS crosslinked electrospun regenerated tussah silk fibroin nanofiber mats

The Production of Soluble Regenerated Silk Fibroin Powder with High Molecular Weight and Silk Protein-Based Materials

A New Approach for Preparing Chitosan Fibers from a LiOH/urea Solvent System

Structure and properties of regenerated Antheraea pernyi silk fibroin in aqueous solution

Dissolution and regeneration of non-mulberry Eriogyna Pyretorum silk fibroin

Characterization of undegraded and degraded silk fibroin and its significant impact on the properties of the resulting silk biomaterials

A novel method to prepare tussah/ Bombyx mori silk fibroin-based films

Dissolution and processing of silk fibroin for materials science

A Solvent System Involved Fabricating Electrospun Polyurethane Nanofibers for Biomedical Applications

Heat-Insulated Regenerated Fibers with UV Resistance: Silk Fibroin/Al2O3 Nanoparticles

Dissolution Behavior and Structural Changes of Silk Fibroin in Calcium Chloride-Ethanol-Water Solvent Systems

Preparation and characterization of novel nanocomposite films formed from silk fibroin and nano-TiO2

Regenerated Bombyx silk solutions studied with rheometry and FTIR

Preliminary exploration of the artificial preparation, structures and properties of regenerated silk fibers

Effect of Nano Titanium Dioxide on Mechanical Properties of Regenerated Silk