The Tune Effect of Surface Pt/Mo Ratio on the Stability and Morphology of α-MoC surfaces
Juhui Gong,Ruiqin Sun,Linxia Cui,Cheng Cao,Ke Shi,Mingyuan Zhang,Rui Gao,Haigang Hao
DOI: https://doi.org/10.1016/j.surfin.2020.100831
IF: 6.2
2021-02-01
Surfaces and Interfaces
Abstract:<p>The influence of the loaded-Pt atoms on the stability and morphology of α-MoC haven't been studied before, which is important for developing high-performance Pt/MoC catalyst. Hence, seven surfaces of α-MoC with ten terminals were selected to research the effects of Pt/Mo ratio on the stability and morphology of α-MoC under CH<sub>4</sub>/H<sub>2</sub> and CO/CO<sub>2</sub> atmospheres. The calculations demonstrate that although the stability of all the surfaces are increased with the increasing of Pt/Mo ratio, only few facets could be exposed under the research conditions. At low Pt/Mo ratio, (113)-Mo is the only exposed surface at 0K and 600K, while a certain proportion of (100) surface appears at 1000K under CH<sub>4</sub>/H<sub>2</sub>; (113)-C is the only exposed surface at 0K, whereas the (100) is the exclusive surface at 600K and 1000K under CO/CO<sub>2</sub>. At high Pt/Mo ratio, the influence becomes obvious. Under CH<sub>4</sub>/H<sub>2</sub>, the exposed surface was tuned from (113)-Mo to (111)-Mo at 0K, the (100) facets disappears at 1000K, while the (113)-Mo surface is unchanged at 600K. Under CO/CO<sub>2</sub>, the (113)-C surface is still the only exposed surface at 0K, which changes into (100), (012) and (113)-C at 600K, and into (100), (012) and (113)-Mo at 1000K.</p>
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films