Abstract:PbS hollow spheres were successfully prepared by a sodium citrate-assisted hydrothermal process at 120 degrees C for 12 h, employing lead acetate trihydrate, thiourea and sodium citrate as precursors. The diameter of PbS hollow spheres is 200-400 nm, which is composed of about 50-80 nm nanoparticles. The synthesized product was characterized by powder X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), Fourier transform-infrared (FT-IR) spectroscopy, ultraviolet-visible spectrometer (UV-vis) and near-infrared absorption spectrometer (NIR). The effects of the reaction conditions on morphologies of PbS structures were investigated. Star-shaped and flat PbS crystals were obtained by changing some experiment conditions. The results show that temperature, sodium citrate concentration, sulfur sources and solvent play key roles on the final morphologies formation of PbS crystals. Especially, ED result indicates that PbS hollow spheres hold single crystal-like electron diffraction patterns. And the possible formation mechanism of hollow spheres was proposed.

Synthesis of Sb2S3 Peanut-Shaped Superstructures

Tartatric Acid and L-Cysteine Synergistic-Assisted Synthesis of Antimony Trisulfide Hierarchical Structures in Aqueous Solution

Hierarchical Construction of PbS Architectures Based on the Adsorption and Sustained Release of H2S by TBAB

HYDROTHERMAL SYNTHESIS OF DENDRITE-LIKE ZINC SULFIDE CRYSTALS

Sonochemical method for the synthesis of antimony sulfide microcrystallites with controllable morphology

Preparation of Shuttle‐like Sb2S3 Nanorod‐bundles Via a Solvothermal Approach under Alkaline Condition

Benzene-thermal synthesis and characterization of ultrafine powders of antimony sulfide

Shape Controllable Preparation and Characterization of Hierarchical PbS Submicron Cubes Via a Solvothermal Method

Hydrothermal synthesis of PbS hollow spheres with single crystal-like electron diffraction patterns.

Surfactant-Assisted Controlled Synthesis of Antimony and Bismuth Three-Dimensional Superstructures in Different Hydrothermal Emulsion Systems

Hydrothermal synthesis of M2S3 (M = Sb, Bi) bulk single crystals and nanorods

A facile hydrothermal method to synthesize Sb2S3/Sb4O5Cl2 composites with three-dimensional spherical structures

Shape-Controlled Syntheses of Pbs Submicro-/Nano-Crystals Via Hydrothermal Method

Antimony Sulfide Tetragonal Prismatic Tubular Crystals

Solvothermal growth of Sb2S3 microcrystallites with novel morphologies

L-Cysteine-Assisted Tunable Synthesis of PbS of Various Morphologies

Hierarchical, Star-Shaped Pbs Crystals Formed by A Simple Solution Route

The synthesis of SbSI rodlike crystals with studded pyramids

Microwave-Assisted Synthesis Of Sb2se3 Submicron Tetragonal Tubular And Spherical Crystals

Liquid-liquid interfacial synthesis of single-crystalline PbS nanoplates and nanocube-based microspheres

Synthesis of Bismuth Sulfide Nanorods in Acidic Media at Room Temperature