Corrosion Behavior of TiO2 Film Prepared by Anodic Oxidation Method in Simulated Deep Sea Hydrothermal Region

张勤杰,姚文红,贺本林,葛洪仑,孙苗,刘威,曲俊,王玮
2013-01-01
Abstract:TiO_2 films were formed on metallic titanium substrate by anodic oxidation method,and its corrosion resistance was studied in simulated deep sea hydrothermal region by hydrothermal synthesis reactor.The crystal form,chemical composition,microstructure and hydrophobic properties of oxide film and products of corrosion sample were characterized by X-ray diffraction (XRD),scanning electron microscopy(SEM) and water contact angle tester,respectively.Their electrochemical properties were investigated through polarization curves.The results showed that in the simulative deep sea hydrothermal system,the non-compact TiO_2 film which was produced on the surface of Ti and anodic oxidation sample could not protect the substrates well and the non-compact TiO_2 film was different from the anodic oxidation TiO_2 film.The corrosion potential of Ti electrode shifted 0.45 V towards negative direction and TiH_2 formed on the surface of Ti after corrosion,while the corrosion potential of Ti sample processed by anodic oxidation method changed less,and no TiH_2 was produced on its surface.The above results indicated that the TiO_2 films formed on metallic titanium substrates by anodic oxidation method had a good corrosion resistance.
What problem does this paper attempt to address?