Absorbable biomembrane in the regeneration of mucoperiosteum of the hard palate
En Luo,Jing Hu,Ji-hua Li,Qiu Ning,Lan Yu,Shi-cheng Wei
DOI: https://doi.org/10.3321/j.issn:1673-8225.2005.42.017
2005-01-01
Abstract:Aim: To evaluate the role of PDLLA biofilm as guide to regeneration of the soft tissue defects in the palates of goats. Methods: The experiment was done in the Animal Experiment Center of West China Basic Medical College, Sichuan University, during March to July 2004. Twelve goats as experimental animals were divided into PDLLA experimental group and blank control group at random. PDLLA biofilms (molecular weight, 4.1×10 4 D; stress strength, > 5.0 MPa; 0.5 mm in thickness; colorless and transparent) were supplied by Dikang Biomedical Co., Ltd. 18.0 mmx16.0 mm rectangle mucoperiosteum and 17.0 mm×15.0 mm bone were removed in mid part of the hard palates. The oral and nasal cavity were communicated each other and the perforating model of palate defect was established. 21.0 mm×19.0 mm PDLLA biofilms were implanted into the defects of the experimental group. The same size defect was established in the blank control group, but no biofilms were implanted. The soft tissue defects of two groups were measured 1-7 weeks after the operation. The regenerating soft tissue in the defects was observed histologically 7 weeks after the operation. Results: All the 12 goats i n the experiment were brought into the result analysis. 1 The defect area comparison between the two groups at different time: Compared with the blank control group, the defect area of PDLLA experimental group significantly decreased in 3,4,5,6 weeks [(249.11 ±26.08), (202.32 ±14.15); (249.11 ±28.34), (167.32 ±22.73); (249.11±27.23), (72.14±12.08); (249.11±26.78), (3.34±2.28)mm 2, P < 0.01], and the mucoperiosteal defects were closed in 7 weeks. 2 The comparison of general observation: In the PDLLA experimental group, the operating area was red and swelling in the 1st week, but the abnormal disappeared in the 2nd week. The defect area decreased slightly and the biofilms became chalky and semitransparent in 1 and 2 weeks. The defect area decreased continuously in 3, 4, 5 weeks, and the biofilms became chalky and opacity. In the 6th week, the mucoperiosteal defects were completely closed in 5 of all the 6th goats, and the defect was closed in the left goat in the 7th week. The scar tissue could be observed in the regenerating tissue. In the blank control group, the operating area was not red and swelling in the 1st week. The epithelium regenerated and completely covered the edge of defect in the 2nd week. The mucoperiosteum regenerated into nasal cavity and covered the edge of bone defect. The defect area did not decrease in 3, 4, 5, 6, 7 weeks. The permanent fistula between oral cavity and nasal cavity occurred in all the 6 goats. 3 The light microscope observation: The regenerating tissue was covered with multilayer squamous epithelium and the deferent size scar tissue could be observed. The fibers of epithelium and connective tissue were irregular in the thin regenerating tissue and regular in deferent layers of the thick regenerating tissue. The blood vessel could be observed in the connective tissue, and no nerve, muscle or bone was observed. The irregular envelope of tight connective tissue formed around the biofilms. No obvious inflammation and foreign body reaction were observed. Conclusion: PDLLA biofilm can guide the regener ation of mucoperiosteal tissue to close the limited size palatal defects, and to reconstruct the palate soft tissue.