Preparation and Magnetic Properties of Fe3O4/wood Composite

GAO Hong-lin,WU Guo-yuan,ZHANG Gen-lin,GUAN Hong-tao,YANG Xiang-jun,LAN Yao-zhong

2010-01-01

Abstract:Fe3O4/wood composites were prepared by the in-situ chemosynthesis method at room temperature with Yunnan fir wood as the matrix and mixed solution of FeCl3 and FeCl2 as the impregnating solution.The structure characterized by X-ray diffraction(XRD),and scanning electron microscopy(SEM)shows that the average particle size of Fe3O4 crystal is about 14nm,but the particles settled in the hole of wood are aggregated with the size changed to 0.5-2.5μm.Fourier transform infrared(FT-IR)analysis indicates that there exists interaction between Fe3O4 particles and the wood matrix,and the interaction influences the magnetic property of the composite.The magnetic feature was characterized by vibrating sample magnetometer(VSM).The results show that the concentration of impregnating solution and the wood fiber direction has some effects on the magnetization.It is found that the magnetization of the composite reaches to its maximum value with Fe ion concentration of 1.2mol/L in the impregnating solution.Samples under the magnetic field with the same direction as their fiber directions have higher remain magnetization.