Abstract:In this study, a series of Li1-xNaxBi (MoO4)2: 0.3 Yb3+, 0.01Ho3+ (x = 0–1) phosphors were prepared using a high-temperature solid-state reaction method. The as-prepared sample produced high-intensity green light (542 nm) and weak red light (646 nm) under the excitation of a 980 nm laser, which was generated by the radiative relaxation of 5S2/5F4→5I8 and 5F5→5I8 energy levels in Ho3+. We performed X-ray diffraction (XRD) tests on our samples, the XRD test data show that the incorporation of Yb3+ and Ho3+ shrank the lattice, and the luminescence intensity improved after doping with Na+. With an increase in Na+ concentration, two inflection points were observed in the luminescence intensity. The luminescence intensity was strongest when the Na+ concentration was 30% and 80%; moreover, it was also the inflection point of the 2θ value of the strongest diffraction peak (112) of the sample. By fitting the pump power and the up-converted luminescence intensity, it was inferred that the emission of one photon at 542 and 646 nm requires the absorption of three photons. Using the fluorescence decay time test, it was observed that the 2θ value corresponding to the strongest diffraction peak of the sample had a corresponding relationship with the fluorescence lifetime. Therefore, this study provides a reference for the further exploration of ion substituted upconversion luminescent materials.

Influences of Mg2+ Ion on Dopant Occupancy and Upconversion Luminescence of Ho3+ Ion in Linbo3 Crystal

Investigations on Defect Structure and Light-Induced Scattering of Mg:Ho:Linbo3 with Various Mg2+ Concentration

Effect of Ho3+ and Tm3+ Concentration on UV-VIS-NIR and Upconversion Luminescence in Ho:Tm:LiNbO3 Crystals

Dopant Occupancy And Optical Properties Of Ho3+ In Hf: Ho: Linbo3 Crystal

Luminescent Enhancement in Mg- and Er-Codoped Linbo3 Crystals

Controllable and White Upconversion Luminescence in Linbo3:Ln(3+) (ln = Ho, Yb, Tm) Single Crystals

Upconversion Photoluminescence And Exafs Of Er3+ And Ho3+ Codoped With Li+ Ion

Influence of Nd<SUP>3+</SUP> ions on the emission of Ho<SUP>3+</SUP> ions-doped NaY<sub>0.1</sub>Gd<sub>0.9</sub>(WO<sub>4</sub>)<sub>2</sub> crystal at 2.0 m

Upconverted Photoluminescence in Ho3+ and Yb3+ Codoped Gd2o3 Nanocrystals with and Without Li+ Ions

MgO-codoping Effects on the Spectroscopic Properties of Er3+-doped LiNbO3

White-light manipulation in Ho3+/Yb3+/Tm3+-doped LiNbO3 single crystals through transition metal Mn2+ ion doping

Enhance upconversion photoluminescence intensity by doping Li+ in Ho3+ and Yb3+ codoped Y2O3 nanocrystals

Influence of MgO codoping on the optical properties of Er 3+ -doped near-stoichiometric LiNbO 3

Effects of Na+-doping on the structure and luminescence properties of Li1-xNaxBi(MoO4)2: Yb3+/Ho3+ phosphors

The effect of Mg2+ ions in Er3+,Tm 3+-codoped LiNbO3 single crystal

Influence of Oxygen Vacancy on the Fluorescence of Nd:Mg:liNbO 3 and Er:Mg:Nb0 3 ;, Crystals

Enhancement of Er3+ Luminescence in LiNbO3:Mg Crystals

Influence of MgO codoping on the optical properties of Er<sup>3+</sup>-doped near-stoichiometric LiNbO<sub>3</sub>

Upconversion White-Light Emission in Ho3+/Yb3+/Tm3+ Codoped Linbo3 Polycrystals

Effects of Nd Ions on the Fluorescence Properties of Ho: BaY2F8 Crystals in the Wavelength Range of 1–2.5 Μm

Dopant occupancy and optical properties of Er 3+ in Er/Zn-codoped lithium niobate crystal