Abstract:In order to test effect of the compound additive on temperature, heavy metal volatilization and toxicity of leaching heavy metals in slag, a melting and solidification process was carried out using own developed compound additive on fly ash from a northern city domestic waste incinerator. The results show that the additive can effectively decrease the melting temperature of fly ash from 1 320 ℃ to 1 160 ℃ , and enhance the volatilization of some heavy metals in fly ash. When temperature was 1 000 ℃, the volatilization of Cr, Zn, Pb and Cd increased 24. 1%, 30. 3%, 18. 8% and 20% respectively. When temperature was 1 350 ℃, the volatilization of Cu was 93. 5%. And the content of heavy metals in slag was reduced greatly, then the leaching concentration of heavy metals in slag can meet the limit value prescribed by national standard. The operation parameters were that the proportion of compound additive was 5%, the flow rate of air which as carrier gas was 250 mL/min; melting time was one hour.

Effect of Compound Additive on Melting and Solidification of Fly Ash from Waste Incinerator