Multiphoton Upconversion Fluorescence Properties of Heteroaromatic Push-Pull Polymer

Qian Ying,Yu Wen-Jie,Lue Chang-Gui,Zhu Xiao-Qin,Cui Yi-Ping

DOI: https://doi.org/10.3866/pku.whxb20090613

2009-01-01

Abstract:Two novel heteroaromatic push-pull fluorescence polymers poly [(2,5-diphenylene- 1,3,4-oxadiazole)4,4'-vinylene-alt-N,N'-bis(4-phenylenevinylene)-phenylamine] (P-1) and poly [(2,5-diphenylene-1,3,4-oxadiazole)-4,4'-vinylene-alt-N-ethyl-3,6-carbazolevinylene] (P-2) were synthesized by the Wittig reaction and the Heck reaction. Polymers P-1 and P-2 have decomposition temperatures of 373 and 412 degrees C, respectively, and exhibit good thermal stabilities. Their electrochemical properties were explored by cyclic voltammetry. The highest occupied molecular orbital (HOMO) energy levels of P-1 and P-2 were -5.39 and -5.81 eV, respectively, and the lowest unoccupied molecular orbital (LUMO) energy levels of P-1 and P-2 were -2.81 and -3.09 eV, respectively. Three-photon and two-photon upconversion fluorescence spectra of both polymers were measured using a femtosecond Ti:sapphire that was pumped by a femotosecond laser at 1.250 and 800 nm. Strong three-photon upconversion fluorescence with maximum emission wavelengths of 510 nm for P-1 and 491. nm for P-2 in THF solution were observed. By pumping at 800 nm, strong two-photon upconversion fluorescences at 511 nm for P-1 and 495 nm for P-2 in THF were measured. Maximum peaks of single-photon fluorescence in THF were at 503 nm for P, and at 475 nm for P-1 with fluorescence quantum yields of 0.80 for P-1 and 0.31 for P-2. The effect of solvent polarity on multi-photon fluorescence was studied. Increased solvent polarity were found to induce a marked red-shift of the emission band in polymers P-1 and P-2.