Oriented growth of magnetite along the carbon nanotubes via covalently bonded method in a simple solvothermal system
Yingqing Zhan,Rui Zhao,Fanbing Meng,Yajie Lei,Jiachun Zhong,Xulin Yang,Xiaobo Liu
DOI: https://doi.org/10.1016/j.mseb.2011.03.010
2011-01-01
Abstract:A new type of CNTs/magnetite hybrid material was prepared via covalently bonded method in a simple solvothermal system using FeCl 3 as iron source, ethylene glycol as the reducing agent, and 4-aminophenoxyphthalonitrile-grafted CNTs as templates. The magnetite nanoparticles, with the diameters of 70–80 nm, were self-assembled along the CNTs. The FTIR, UV–vis and DSC revealed that a stable covalent bond between nitriles group and iron ion promoted the oriented growth of magnetite nanoparticles along the CNTs, resulting in good dispersibility and solution storage stability. The magnetic properties measurements indicated that a higher saturated magnetization (70.7 emu g −1 ) existed in the CNTs/magnetite hybrid material, which further enhanced the electromagnetic properties. The magnetic loss was caused mainly by natural resonance, which is in good agreement with the Kittel equation results. The novel electromagnetic hybrid material is believed to have potential applications in the microwave absorbing performances. Keywords Carbon nanotubes Magnetite Phthalocyanine Nanostructured materials Bonding Properties 1 Introduction Carbon nanotubes (CNTs) discovered by Iijima [1] , have attracted more and more attention for their outstanding electronic, mechanical, thermal, chemical properties and significant potential applications in nanoscience and nanotechnology [2] . Due to their fascinating nanoscale dimensions and high surface areas, CNTs are considered as an ideal carrier to assembly of inorganic nanoparticles which have special properties [3–7] . Among these inorganic nanoparticles, magnetite nanoparticles have long been of scientific and technological interest because of their unique magnetic and electric properties [8–11] . In recent years, a range of CNT-magnetite hybrid materials have been fabricated and show potential applications in polymeric materials, nanoprobes for magnetic force microscopy, wastewater treatment, biosensors, and drug delivery [12–15] . Several approaches, such as hydrogen bonding, in situ growth, covalent linkage and electrostatic interaction have been developed to fabricate CNTs/magnetite hybrid materials. According to these approaches, either the nanoparticles or CNTs (or both) need modification with functional groups. Therefore the types of functionalization and the strength of interaction determine the dispersibility, solubility and properties of the hybrid materials. It is well known that metal phthalocyanine (MPc) have attracted much attention for many years because they exhibit unique properties [16] . The metal phthalocyanine molecules (denoted as MPc, hereafter) comprise a very stable π-conjugated macrocyclic ligand that incorporates a metal ion in the void at the center of the molecule. Therefore, MPc possess good solubility in many solvents, chemical and thermal stability. As a matter of fact, covalent attachment of metal phthalocyanine (MPc) on the surface of carbon nanotubes have been reported elsewhere and exhibit new optical, magnetic and electrical properties [17–19] . In view of these, covalent attachment of magnetite inorganic nanoparticles on the carbon nanotubes with MPc is of high interest. In this paper, we present a facile approach to obtain CNT/magnetite hybrid material based on the covalent bond between the templates of 4-aminophenoxyphthalonitrile-functionalized CNTs and iron ion in a solvothermal system. A very stable covalent bond between nitriles group and iron ion promoted the oriented growth of magnetite nanoparticles along the CNTs. This approach promised good dispersibility and solution storage stability of resulting hybrid material. The as-prepared CNTs/Fe 3 O 4 hybrid material possessed higher saturated magnetization and electromagnetic properties, which was believed to have potential applications in the microwave absorbing area. 2 Experimental 2.1 Materials CNTs (diameters: 10–30 nm, purity: > 95%) were supplied by Chengdu Organic Chemistry Co. Ltd., Chinese Academy of Sciences. FeCl 3 ·6H 2 O (99%), ethylene glycol (99%) and polyethylene glycol (99%) were purchased from Kelong regent Co. Ltd., Chengdu, China. All the chemicals and reagents were used without further purification. 4-Aminophenoxyphthalonitrile was synthesized and purified according to the procedure reported before [20] . 2.2 Chemical modification of CNTs The chemical modification of CNTs was prepared as follow. CNTs were sonicated in a mixture of concentrated sulfuric and nitric acid (3:1 by volume) for 2 h at 50 °C. The obtained carboxyl-terminated CNTs were then refluxed in excess SOCl 2 at 70 °C for 72 h. The excess SOCl 2 was removed by distillation and remaining solid was dried in vacuum. The obtained solid was reacted with 4-aminophenoxyphthalonitrile in 100 mL N , N -dimethylformamide at room temperature for 72 h. The excess 4-aminophenoxyphthalonitrile was removed completely by washing with dichloromethane and acetone, giving a black solid after filtration. 2.3 Preparation of phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material Typical synthesis of phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material was carried out in a solvothermal system by reduction reactions between FeCl 3 and ethylene glycol in the presence of 4-aminophenoxyphthalonitrile-grafted CNTs. 1.94 g FeCl 3 ·6H 2 O was dissolved into 200 mL ethylene glycol, followed by addition of 5.0 g polyethylene glycol and 0.5 g 4-aminophenoxyphthalonitrile-grafted CNTs to form a black solution with the help of an ultrasonic bath. After that, 18 g NaAc was slowly added into the solution with vigorous stirring at 60 °C for 2 h. The mixture was sealed in a Teflon-lined stainless steel autoclave and maintained at 200 °C for 15 h, and cooled to room temperature. The black products were rinsed with ethanol for several times, and dried at 60 °C for 8 h. As a reference, the CNTs/Fe 3 O 4 hybrid material without covalent bond was synthesized according the above method and compared with the above phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material. 2.4 Characterization The synthesized products were characterized by fourier transform infrared spectrometer in KBr pellets (FTIR) (NICOLET MX-1E), differential scanning calorimetry (DSC) (DSC Q100, TA Instruments), X-ray diffraction (XRD) (Rigaku RINT2400 with Cu Kα radiation), scanning electron microscopy (SEM) (JSM, 6490LV) and transmission electron microscopy (TEM) (Hitach, H600). Magnetic study was performed by a vibrating sample magnetometer (VSM, Riken Denshi, BHV-525). Electromagnetic (EM) parameters were measured by a vector network analyzer (Agilent 8720ET), in which the GNs/Fe 3 O 4 hybrid material was mixed with paraffin at certain mass filling ratio (30 wt%) and compressed to standard ring shapes (outer diameter: 7 mm, inner diameter: 3 mm,thickness: 2–4 mm). 3 Results and discussion The reaction for chemical modification of carbon nanotubes is shown in Fig. 1 a . It is well known that treating the CNTs with oxidizing acids could create considerable functional groups such as carboxyl on the out surface of CNTs which become negatively charged. Chemical modification of CNTs by SOCl 2 was thus obtained by substitution reaction at 70 °C. The obtained solid was further reacted with 4-aminophenoxyphthalonitrile via another substitution reaction. So the phthalonitrile was chemically bonded to the CNTs surface. Fig. 1 b shows the illustration of synthesis process of CNTs/Fe 3 O 4 hybrid material. According to the previous reference [21] , the hierarchical Fe 3 O 4 microspheres could be formed in solvothermal system by reduction reaction between FeCl 3 and ethylene glycol in the presence of PEG. It well-known that ethylene glycol plays an important role in ferrite formation. Ethylene glycol is a strong reducing agent with a relatively high boiling point, and has been widely used in the polyol process to provide fine metal and metal oxide nanoparticles. In this paper, some of the ferric ions were first in situ reduced into Fe 2+ ions in the solvothermal process and then coprecipitated into Fe 3 O 4 crystallites. On the other hand, after grafted by 4-aminophenoxyphthalonitrile, modified CNTs could be treated as a kind of phthalonitrile precursor. As the solvothermal process went on, the ferric ions on the surface of the Fe 3 O 4 were further strongly bonded with the 4-aminophenoxyphthalonitrile-grafted CNTs in the presence of high boiling point solvent ethylene glycol. Therefore the phthalocyanine was formed and oriented growth of Fe 3 O 4 nanoparticles along the carbon nanotubes via covalent bond was realized. In our cases, the formation of Fe 3 O 4 nanoparticles was through an aggregation process of tiny nanocrystallites on the surface of CNTs template. When the Fe 3 O 4 hybrid grew to a critical size, the PEG 2000 would act as a stabilizer to prevent the further aggregation. The nature of the chemical groups on surface of CNTs was investigated by FTIR spectra shown in Fig. 2 . After acid treatment, CNTs exhibited two absorption bands at 3420 and 1730 cm −1 ( Fig. 2 a), which were induced by the carboxyl and hydroxyl attached to the open ends of CNTs. Carboxyl-terminated CNTs were further chemically modified by SOCl 2 and 4-aminophenoxyphthalonitrile. As seen from Fig. 2 b, the absorption band at 1637 cm −1 was assigned to the C O stretching of the amide bond (–NHCO–). Four bands at 2923, 2852, 1507, 1586 cm −1 are the characteristics of benzene ring. Another feature should be given attention is that the peak at 2230 cm −1 is characteristic of –CN. All this observations indicated that the 4-aminophenoxyphthalonitrile has been grafted onto the CNTs successfully. In the FTIR spectra of final product ( Fig. 2 c), we can observe that absorption band at 580 cm −1 is assigned to the characteristic peak of Fe 3 O 4 . Meanwhile, there are other peaks characteristic of phthalocyanine macrocycles, i.e. 1383, 1010 and 909 cm −1 [18] , and the characteristic absorption peak of cyano group at 2230 cm −1 disappeared after the 4-aminophenoxyphthalonitrile-functionalized CNTs reacted with iron ion during the solvothermal process. These observation revealed that a very stable interaction between nitriles group and iron ion happened during the solvothermal process, which promoted the oriented growth of Fe 3 O 4 nanoparticles along the carbon nanotubes. The results of FTIR analysis are well consistent with the UV–vis spectra, in which the characteristic absorption bands of the hybrid material at 680–703 cm −1 were attributed to the iron phthalocyanine. Fig. 3 shows the DSC curves of 4-aminophenoxyphthalonitrile-grafted CNTs and phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material. Compared with the 4-aminophenoxyphthalonitrile-grafted CNTs ( Fig. 3 a), a new reaction peak at 320 °C was detected in the CNTs/Fe 3 O 4 hybrid material, as shown in Fig. 3 b, which was attributed to the curing reaction of iron phthalocyanine. All these findings are indicative of the formation of a covalent bond between Fe 3 O 4 and 4-aminophenoxyphthalonitrile-grafted CNTs. Fig. 4 shows the XRD pattern of phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material. The diffraction peak at 2 θ = 26.24° is assigned to (0 0 2) plane of CNTs. After surface decoration, six new peaks at 30.1°, 35.5°, 43.1°, 53.4°, 56.9°, and 62.4° were observed. The positions and relative intensities of these non-CNTs related new peaks match well with the (2 2 0), (3 1 1), (4 0 0), (4 2 2), (5 1 1), (4 4 0) planes of the standards XRD data for the cubic spinal crystal structure of bulk magnetite (JCPDS file No. 19-0629). So it could be concluded that a kind of magnetite-CNT heterostructure was formed during the solvothermal process. The morphology and structure of as-prepared CNTs/Fe 3 O 4 hybrid material were investigated by SEM and TEM. It can be seen from Fig. 5 a and b that the magnetite nanoparticles, with the diameters of 70–80 nm, are self-assembled along the surface of CNTs. It is noticeable that the formation of nanoparticles is selective to the sidewalls of CNTs via covalent bond and most of Fe 3 O 4 nanoparticles are attached on the outer surface of CNTs. Because of the adverse influence of the extremely high curvature of CNTs [22] , the distributing of these nanoparticles revealed a little non-uniformity. Nonetheless, the size and size distribution is more easily controlled compared to the non-covalent method, as seen in Fig. 5 c. These observations indicated that our method is of high efficiency. To examine solubility and solution storage stability, the as-synthesized CNTs/Fe 3 O 4 hybrid material can be easily dispersed in ethanol and remains very stable for at least 4 weeks at room temperature, while the breakdown is detected in the CNTs/Fe 3 O 4 hybrid material without covalent bond. Such characteristic is beneficial to widen the CNTs/Fe 3 O 4 hybrid material's application in many areas. The enhanced dispersibility and solution storage stability of the as-prepared hybrid material was due to the strong and stable covalent bond interaction between the Fe 3 O 4 and 4-aminophenoxyphthalonitrile-grafted CNTs. And the solubilization mechanism involved π–π interactions between the side walls of the CNTs and the aromatic compounds [23] . The magnetic properties of CNTs/Fe 3 O 4 hybrid materials were investigated at room temperature using a vibrating sample magnetometer with an applied field of −6000 Oe ≤ H ≤ 6000 Oe. The magnetic hysteresis curve of the sample measured at 300 K illustrates the strong magnetic response to a varying magnetic field ( Fig. 6 a) . The saturation magnetization value of phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material is 70.7 emu g −1 , which is much higher than that of CNTs/Fe 3 O 4 without covalent bond ( Fig. 6 b). It is well-known that aggregates made from magnetic particles show demagnetizing effect due to random dipole–dipole interaction between particles resulting in antiferromagnetically coupling [24,25] . So the enhancement of the magnetic properties was attributed to the better dispersion behaviors of the magnetic particles attached on the surface of the CNTs, in agreement with the SEM and TEM discussion. Fig. 7 a and b shows the frequency dependence of the real ( ɛ ′) and the imaginary parts ( ɛ ″) of the relative complex permittivity of two kinds of CNTs/Fe 3 O 4 hybrid materials. It can be found that the values of ɛ′ and ɛ ″ of phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material declined from 49.82 to 28.20 and from 26.18 to 7.82, respectively, with increasing frequency in the 1–18 GHz. According to free electron theory [26] , ɛ ″ = 1/2 ɛ 0 πρƒ , where ρ is the resistivity. It indicated the higher resistivity of the hybrid material compared with the CNTs/Fe 3 O 4 hybrid material without covalent bond. This was attributed to the effective dispersion and relatively low electrical behavior of phthalocyanine existed in the hybrid material. In general, the high electric resistivity and proper dielectric loss are favorable to the improvement of the microwave absorption properties. Fig. 7 c and d shows the complex permeability (real part (c) and imaginary part in (d)) of the two kinds of hybrid materials in the frequency of 0.5–18 GHz. It is found that the real part of the two kinds of hybrid materials exhibited an abrupt decrease in the 0.5–4 GHz and retained an approximate constant of about 0.9 over 4–18 GHz. The real part of relative permeability of the phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material is higher than that of hybrid material without covalent bond in the range of 0.5–4 GHz. Fig. 7 d shows the frequency dependence imaginary part of permeability μ ″ of the two kinds of hybrid materials, which shows resonance peaks near 1.15 GHz. The Kittel equation has been widely used to calculate the natural resonance frequency of magnetite materials; the natural resonance of the sphere-shaped magnet is [27] . f r = γ H a where γ = 28 GHz T −1 , is the gyromagnetic ratio and Ha = 4| K 1 |/3 μ 0 M s is the effective anisotropy field. The saturation magnetization μ 0 M s is 0.542 T and the anisotropic coefficient K 1 for the fcc-type bulk magnetite is about −9 × 10 3 J m −3 , so the theoretical calculation of the natural resonance frequency should be γ Ha ≈ 1.2 GHz, which matches well with the experimental data of 1.16 GHz. This demonstrates that the as-synthesized products show mainly sphere-like morphology and the magnetic loss is caused mainly by the natural resonance in the microwave region. Meanwhile, the higher value of μ ″ of the phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material, as shown in Fig. 7 d, is due to its higher saturation magnetization and good dispersibility. The magnetic loss also can explain why phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material had better electromagnetic properties (see the inset of Fig. 7 d). It can be seen that the magnetic loss of as-prepared hybrid material was higher than that of hybrid material without covalent bond, over the 0.5–18 GHz frequency range. 4 Conclusions In summary, a new type of CNTs/Fe 3 O 4 hybrid material has been successfully prepared via covalently bonded method in a simple solvothermal system. Formation, structure, magnetic and electromagnetic properties of the as-prepared hybrid material were investigated. Chemical bonded by phthalocyanine, CNTs/Fe 3 O 4 hybrid material would significantly improve its dispersibility and solubility in common solvents. The results suggest that phthalocyanine covalently bonded CNTs/Fe 3 O 4 hybrid material has enhanced the magnetic and electromagnetic properties. The novel electromagnetic hybrid material is believed to have potential applications in the microwave absorbing performances. References [1] S. Iijima Nature 354 1991 56 58 [2] R.H. Baughman A.A. Zakhidov W.A. de Heer Science 297 2002 787 792 [3] Y.J. Lei R. Zhao Y.Q. Zhan F.B. Meng J.C. Zhong X.L. Yang X.B. Liu Chem. Phys. Lett. 496 2010 139 142 [4] M.M.J. Treacy T.W. Ebbesen J.M. Gibson Nature 381 1996 678 680 [5] M.J. O’Connell S.M. Bachilo C.B. Huffman V.C. Moore M.S. Strano E.H. Haroz K.L. Rialon P.J. Boul W.H. Noon C. Kittrell J. Ma R.H. Hauge R.B. Weisman R.E. Smalley Science 297 2002 593 596 [6] T.W. Odon J. Huang P. Kim C.M. Lieber Nature 391 1998 62 64 [7] H. Zhu H.Y. Lin H.F. Guo L.F. Yu Mater. Sci. Eng. B 15 2007 101 104 [8] L.T. Qu L.M. Dai E.J. Osawa J. Am. Chem. Soc. 128 2006 5523 5532 [9] Y. Shan L. Gao Mater. Chem. Phys. 103 2007 206 210 [10] K.Y. Jiang A. Eitan L.S. Schadler Nano Lett. 3 2003 275 277 [11] X.G. Hu T. Wang L. Wang Langmuir 23 2007 6352 6357 [12] Z. Deng E. Yenilmez J. Leu J.E. Hoffman E.W. Straver H. Dai K.A. Moler Appl. Phys. Lett. 85 2004 6263 6265 [13] H.T. Wang L.L. Gao S.C. Yan N.P. Huang Z.D. Xiao Mater. Sci. Eng. B 25 2009 191 194 [14] D. Shi J.P. Cheng F. Liu X.B. Zhang J. Alloys Compd. 502 2010 365 370 [15] F. Stoffelbach A. Aqil C. Jerome R. Jerome C. Detrembleur Chem. Commun. 36 2005 4532 4533 [16] J. Wang W.J. Blau Chem. Phys. Lett. 465 2008 265 271 [17] X.B. Wang Y.Q. Liu W.F. Qiu D.B. Zhu J. Mater. Chem. 12 2002 1636 1639 [18] W. Chidawanyika T. Nyokong Carbon 48 2010 2831 2838 [19] S.J. Yaghmour J. Alloys Compd. 486 2009 284 287 [20] G.P. Cao W.J. Chen J.J. Wei W.T. Li X.B. Liu Express Polym. Lett. 8 2007 512 518 [21] R. Zhao K. Jia J.J. Wei J.X. Pu X.B. Liu Mater. Lett. 64 2010 457 459 [22] Y. Liu W. Jiang S. Li F.S. Li Appl. Surf. Sci. 255 2009 7999 8002 [23] A. Baba Y. Kanetsuna S. Sriwichai Y. Ohdaira K. Shinbo K. Kato S. Phanichphant F. Kaneko Thin Solid Films 518 2005 2200 2205 [24] K. Nakata Y. Hu O. Uzun O. Bakr F. Stellacci Adv. Mater. 20 2008 4294 4299 [25] A.F. Gross M.R. Diehl C.K. Beverly E.K. Richman S.H. Tolbert J. Phys. Chem. B 107 2003 5475 5482 [26] X.F. Zhang X.L. Dong H. Huang B. Lv C.J. Choi J. Phys. D: Appl. Phys. 40 2007 5383 5387 [27] C. Kittel Phys. Rev. 73 1948 155 161