Abstract:Ultra-long single-crystalline trigonal selenium submicrotubes were synthesized using a facile one-step solution-phase approach with the assistance of nonionic surfactant Polyoxyethylene(20)sorbitan monolaurate (Tween-20), which turned out to be significant for the formation of ultra-long Se submicrotubes. XRD, Raman, SEM, and TEM were adopted to characterize the morphology, structure and phase composition of the as-prepared Se products. It was found that the length of the obtained Se submicrotubes was over 100 pm. By variation of the experimental parameters, the t-Se spheres, nanowires, and broken microtubes can be prepared. The possible growth mechanism of the ultra-long selenium submicrotubes was explained. In addition, we have also demonstrated that the synthesized Ultra-long t-Se submicrotubes using the Tween-20-assisted approach can electrochemically charge and discharge with the high capacity of 265 mAh/g (corresponding to 0.97 wt % hydrogen in SWNTs) under normal atmosphere at room temperature. Cyclic voltammetry was adopted to investigate the adsorption-ox idation behavior of ultra-long selenium submicrotubes. It was observed that the morphology of the synthesized selenium products had a remarkable influence on their capacity of electrochemical hydrogen storage. These differences in hydrogen storage capacity are likely due to the size and density of tubes as well as the microcosmic morphology of different Se samples. The as-obtained ultralong Se submicrotubes are expected to find wide applications in hydrogen storage, high-energy batteries, and optoelectronic, biologic, and catalytic fields as well as in the studies of structure-property relationships. This simple Tween-assisted approach might be extended to the preparations of one-dimensional nanostructures of tellurium and other anisotropic materials.

Single Crystalline Trigonal Selenium Nanotubes And Nanowires Synthesized By Sonochemical Process

Selenium Nanotubes Synthesized by A Novel Solution Phase Approach

Controllable Synthesis of Trigonal Selenium Nanotubes by Ultrasounnic-assisted Method

Controllable Growth of Se Nanotubes and Nanowires from Different Solvent During the Sonochemical Process

Microfluidic System for Synthesis of Trigonal Selenium Nanowires

FACILE SYNTHESIS AND GROWTH MECHANISM OF TRIGONAL SELENIUM NANOWRIES

Sonochemical Approach to Synthesis of Selenium Nanowires

Preparation of Single Crystal Triangular Selenium Nanostructures and Photoelectric Properties

Nucleation−Dissolution−Recrystallization: A New Growth Mechanism for T-Selenium Nanotubes

One-step fabrication of selenium and tellurium tubular structures

Silver-induced Growth of Selenium Nanowires in Aqueous Solution

Solution-phase synthesis and electrochemical hydrogen storage of ultra-long single-crystal selenium submicrotubes.

Rapid, Large-Scale Synthesis and Electrochemical Behavior of Faceted Single-Crystalline Selenium Nanotubes.

Large-Scale Synthesis And Growth Mechanism Of Single-Crystal Se Nanobelts

Selective Synthesis Of Single-Crystalline Selenium Nanobelts And Nanowires In Micellar Solutions Of Nonionic Surfactants

Deterministic Growth Of Nanostructures And Microcrystals Of Trigonal Selenium Via Vapor Phase Deposition Routes

Micelle-Mediated Synthesis of Single-Crystalline Selenium Nanotubes

Controlled Synthesis of Trigonal Selenium Crystals with Different Morphologies

The Fabrication And Characterization Of Single-Crystalline Selenium Nanoneedles

One-dimensional Sb2Se3 nanostructures: Solvothermal synthesis, growth mechanism, optical and electrochemical properties

Inorganic and Organic Templates‐assisted Solvothermal Synthesis of Trigonal Selenium Microrods