Abstract:The porous magnetic polymer microspheres containing carboxyl group were prepared by modified suspension polymerization by using stryene (St), divinylbenzene (DVB) and methacrylic acid (MAA) as monomers in the presence of magnetic gamma-Fe2O3 which was coated with oleic acid (OA) In this experiment, three modification measures were adopted. First, the surface of the magnetic particles was treated by anionic surfactant OA to improve the hydrophobicity of mciro-size magnetic gamma-Fe2O3 Second, the monomer phase containing surface modified magnetic particles and porogens was sonicated for some time to improve the dispersibility of magnetic gamma-Fe2O3 in the monomer phase and strengthen absorbence of the monomer and initiator on the gamma-Fe2O3 surface. Third, the aqueous phase was added to the monomer phase, and the mixture was sonicated for some time before polymerization to make sure all the magnetic particles can be dispersed in the monomer phase to form stable and uniform droplets which is diffrent from the conventional suspension polymerization with the monomer phase added to the aqueous phase. The pretreatment and polymerization process are as follows: Firstly, 10 - 20 g sample of magnetic particles was added to 200 mL ethanol/water solution (volume ratio = 1), and sonicated in a 250 mL beaker for 0.5 h to eliminate impurities on its surface. Then, the purified magnetic powder and 120 g deionized water were mixed together in a 250 mL I three- necked flask equipped with a stirrer, a condenser and a thermometer. As the mixture heated to 85 degrees C, the OA (2/3 (wt/wt) to magnetic particles) was added dropwise within 15 min and the reaction was kept at pH = 5.5 for I h with vigorous stirring. Afterwards, the resulting materials were isolated by magnetic decantation and washed with deionized water for several times to remove the excess OA. The treated magnetic particles were dried at 50 degrees C for 12 h. Magnetic porous microspheres were prepared by modified suspension polymerization in a 250 mL four-neck, round-bottomed flask fitted with a mechanical stirrer, a thermometer, a reflux condenser and a nitrogen gas inlet tube. The monomer phase which consisted of 15 mL monomers ( St/MAA/DVB = 9/3/3 ( mL)), 0. 2 g AIBN as initiator, 15 mL diluent system ( toluene/ n -heptane = 2/1 ( V/ V)) and surface treated magnetic particles was sonicated for 15min. The aqueous phase (AP) was prepared by addition of 0.48 g HEC, 0. 5 g NaCl and 90 mL deionized water. Then the aqueous phase was added to the organic phase and sonicated for 15 min. Hence, the suspension system was kept at 70 degrees C for 24 h. The polymer produced beads were filtrated and washed with hot distilled water, ethanol and acetone several times to remove water-soluble impurities, followed by soak in 1 mol/L HCI for 48 h and extraction with solvent in a Soxhlet extractor for 24 h to remove the porogens and organic impurities. The purified beads were washed with methanol and distilled water and then dried under vacuum for 24 h. FTIR, SEM, optical microscopy and TG were used to characterize the chemical composition, morphology, size and magnetic particle distribution and magnetic characteristics of magnetic polymer microsphere. FTIR analysis demonstrated that the hydrophobicity of magnetic gamma-Fe,O-3, was improved significantly by chemisorption and esterification after the surface modified by oleic acid.The results of FTIR and optical microscopy analysis demonstrated that the desred polymer was bonded to the surface of gamma-Fe2O3 particles, and the polymer microspheres contained carboxyl groups. But the magnetic particles were not uniformly incorporated in the magnetic microspheres because of the magnetic agglomerating force. The morphology analysis by SEM and optical microscopy confirmed that the composite magnetic gamma-Fe2O3/P(St-DVB-MAA) microsphere had a good sphericity with porous structure and a relatively uniform diameter of about 0. 4 similar to 0. 9 mm. The results of TG analysis indicated the content of magnetite in microspheres was 12. 12 %.

Preparation and characterization of self-dispersible polymeric microspheres

Optimising the Shell Thickness-To-Radius Ratio for the Fabrication of Oil-Encapsulated Polymeric Microspheres

Micron-Size Functional Uniform Pmma Particles by Dispersion Copolymerization in Polar Media

Synthesis and Characterization of PE-b-POEGMA Copolymers Prepared by Linear/Hyperbranched Telechelic Polyethylene-Initiated ATRP of Oligo(ethylene glycol) Methacrylates

Preparation and Characterization of Affinity Polymer Basic Microspheres by Soap-Free Emulsion Polymerization

PEG Based Hyperbranched Polymeric Hollow Nanospheres

Preparation and Superficial Properties of Monodisperse Copolymer Microspheres

Preparation of self-dispersible hairy polymer particles based on ring-opening polymerization of D, L-lactide

Preparation of Microsized Crosslinked Microspheres by Dispersion Copolymerization of Polystyrene/polyethylene Glycol 200-Dimethacrylae

Preparation of monodisperse polystyrene microspheres with different functional groups using soap-free emulsion polymerization

Preparation of Thiol-Modified Hairy Polystyrene Microspheres

Preparation and characterization of polystyrene microspheres in the presence of β-cyclodextrin

Preparation and Performance Evaluation of Self-Cementing Nanoscale Polymeric Microspheres with Salt and Temperature Tolerance

PREPARATION AND CHARACTERIZATION OF MAGNETIC POROUS Γ-Fe2o3/p(st-dvb-maa) POLYMER MICROSPHERES

Preparation of narrow-dispersion or monodisperse polymer microspheres with active hydroxyl group by distillation–precipitation polymerization

Preparation of Polystyrene/Polyacrylamide Core-Shell Microspheres via Microfluidizer-Assistant Emulsification Template Methods for Oil Recovery Enhancement

Synthesis and Formation Mechanism of Large-Size Monodisperse P(Glycidyl methacrylate-Styrene) Microspheres by Batch Dispersion Copolymerization

Synthesis of Monodisperse Crosslinked St-PEG200DMA Copolymeric Microspheres

Preparation and characterization of magnetic porous γ-Fe 2O3/P(St-DVB-MAA) polymer microspheres

Preparation of micron-size crosslinked microspheres by dispersion copolymerization of polystyrene/2,2′-oxy-bisethanol diacrylate

Tailored Surface Properties of Monodispersed Polymer Particles with PCL Hairy Chains Synthesized by Hydroxyl‐initiated Ring‐opening Polymerization