Abstract:A nano-featured tantalum coatings with an average thickness of 800¬†nm and grain size of 50¬†nm were successfully prepared by Selective Electron Beam Melted (SEBM) Ti6Al4V substrates by DC magnetron sputtering technology. The details of the physicochemical properties, corrosion resistance and in vitro biocompatibility of the coating were systematically investigated. Elastic modulus of the nano tantalum coatings was around 123.8¬†GPa and the hardness was 8.08¬†GPa. Compared with uncoated Ti6Al4V matrix, the corrosion potential of the Ta-Ti64 samples was positively shifted and the corrosion current density decreased from 2.07¬†√ó¬†10 ‚ąí7 to 2.85¬†√ó¬†10 ‚ąí8 A¬∑cm ‚ąí2 (0.1¬†mV/s). EIS and PDP results show that the coating enhances the humoral corrosion resistance of Ti6Al4V, which can provide active protection for the substrate to prevent the release of toxic ions caused by long-term corrosion. The mouse osteoblast cell line (MC3T3-E1) is applied in this study for biological evaluation. The optical density at 450¬†nm results showed that the cell proliferation rate of tantalum coated surface was faster than that of Ti6Al4V sheet and pure tantalum sheet. The 5-day cell adhesion density is 1.26 and 1.32 times higher than uncoated Ti6Al4V and pure tantalum respectively. The nano-structured Ta layer significantly improved the initial adhesion of MC3T3-E1 cells and promoted cell proliferation. The corrosion resistance and biocompatibility of Ta coating are not only better than titanium matrix, but also better than pure tantalum. The results prove that tantalum coating is an effective method to modify titanium alloy and holds a great potential value on 3D printed personalized implants application.

Effects of Tantalum Ion Implantation on the Corrosion Behavior of Az31 Magnesium Alloys

Retardation of Surface Corrosion of Biodegradable Magnesium-Based Materials by Aluminum Ion Implantation

Improvement in corrosion resistance and biocompatibility of AZ31 magnesium alloy by NH<sub>2</sub><SUP>+</SUP> ions

In vitro biocompatibility and degradation assessment of tantalum oxide coated Mg alloy as biodegradable implants

Effects of Tantalum Concentration on the Microstructures and Mechanical Properties of Tungsten-Tantalum Alloys

Corrosion Resistance and In Vitro Biological Properties of TiO2 on MAO-Coated AZ31 Magnesium Alloy via ALD

Improvement in corrosion resistance and biocompatibility of AZ31 magnesium alloy by NH2+ ions

Corrosion resistance and biocompatibility of carbon ion implanted AZ31B magnesium alloy

Effects of Sodium Tungstate on Properties of Micro-Arc Coatings on Magnesium Alloys

Research on the surface characterization, corrosion and bioactivity of nano-featured tantalum coating on selective electron beam melted Ti6Al4V alloy

The Effect of Ion Implantation Dose on the Friction and Corrosion Performance of Titanium-Coated Magnesium Alloy

Corrosion Resistance of Ag-ion Implanted Mg-Ca-Zn Alloys in SBF

Influence of Titanium Ion Implantation on the Corrosion Behavior of Zircalloy-4 in 1 M H2SO4

Composition of surface layers of titanium VT6 alloy after implantation of tantalum ions

Modification of Corrosion Resistance by Single and Multi-Element Implantation into 304 Stainless Steel

Combined Effects of Tantalum Ion and Gamma Ray Irradiations on MOS Devices with Atomic Layer Deposited $\mathrm{a}1_{2}\mathrm{o}_{3}$ Gate Dielectrics

Influence of titanium ions implantation on corrosion behavior of zircaloy-2 in 1M H 2 SO 4

Modification of Oxidation Resistance of Copper Films by Shallow Implantation

Modification of Corrosion Resistance by Yttrium Ion Implantation of 30 4L Stainless Steel

Effect of Copper Ions Implantation on Corrosion Behavior of Zircaloy-4 in 1 M H2so4

Influence of Biocompatible Metal Ions (ag, Fe, Y) on the Surface Chemistry, Corrosion Behavior and Cytocompatibility of Mg-1ca Alloy Treated with Mevva