Preparation and characterization of organo-montmorillonite antibacterial agents
Ze-peng Jiao,Guan-ke Liang,Li-ling Zhang,Shao-zao Tan,Jia Zheng,Yin Chen
DOI: https://doi.org/10.3969/j.issn.1673-8225.2009.16.028
2009-01-01
Abstract:Background: Ammonium montmorillonite antibacterial agents have been systemically investigated now, but the applications in engineering plastics are limited owing to the low heat resistance. Quaternary phosphonium salts that are high-effective, broad-spectrum and low-toxic bactericidal agents have great heat resistance compared to quaternary ammonium salts. Objective: To explore the structure, surface properties and antibacterial activity of organo-montmorillonite antibacterial agents. Design, Time and Setting: An in vitro observational experiment was performed at Research Laboratory of Department of Chemistry, Jinan University from September to December 2008. Materials: Organo-montmorillonite antibacterial agents were prepared by introducing trimethyldodecyl phosphonium cations into montmorillonite. Methods: The mol ratios of quaternary phosphonium cations to cation exchange capacity of sodium montmorillonite in reaction solutions were 0.51, 1:1 and 1.5:1, respectively, and three kinds of organo-montmorillonite antibacterial agents containing different contents of trimethyldodecyl phosphonium cations were prepared through an ion-exchange method. Main Outcome Measures: The content of quaternary phosphonium cations and heat resistance, the change of interlayer spacing, the zeta potential and the special surface area of samples were measured by using a thermal analyzer, a X-ray diffractometer, a zeta potential analyzer, a specific surface area and porosimetry analyzer, respectively. The minimum inhibitory concentration (MIC) of the samples against Escherichia coli (E. coli) and Staphylococci aureus (S. aureus) was estimated by a two-fold diluting method. Results: The onset temperatures of the decomposition for quaternary phosphonium cations in organo-montmorillonite antibacterial agents were all higher than 300 °C, and they were preferable thermal stability. The interlayer spacing became broader, the zeta potential was more positive, the surface area was lower, and the antibacterial activity was higher when the content of quaternary phosphonium cations increased in organo-montmorillonite antibacterial agents. For the organo-montmorillonite antibacterial agents containing 21.93 wt% of quaternary phosphonium cations, the zeta potential was -19.75 mV, the specific surface area was 47.36 m2/g, and the MIC values against E. coli and S. aureus were 250 and 120 mg/L, respectively. Conclusion: The organo-montmorillonite antibacterial agents containing 21.93 wt% of quaternary phosphonium cations possesses good heat resistance and high antibacterial activity.