Research on Grain Refinement in Bulk Undercooled Fe-Co Base Alloys
Mu Danning,Yang Changlin,Wei Xiaowei,Liu Feng
DOI: https://doi.org/10.3724/sp.j.1037.2012.00286
IF: 1.797
2012-01-01
ACTA METALLURGICA SINICA
Abstract:Fe-Co base alloys, owing to their excellent high tempreture soft magnetic property, have been given more and more attention. Especially, Fe-Co base bulk amorphous-nanocrystalline ma- terials have became an important development direction, while the preparation techniques have limited the wide applications of these high performance magnetic materials. Undercooling rapid solidification technique, independent of the sample size, has unique advantages in preparing bulk microcrystalline and nanocrystalline materials. However, upon large volume of alloy melt, more heterogeneous nucleus and latent heat of crystallization will occurr, which is disadvantageous to obtain a high undercooling and to repress grain growth in the process of solidification. Obviously, regular rapid solidification technique has not met the requirements for the preparation of industrial products with a large volume. So it is important and necessary to combine other rapid solidification techniques with regular rapid solidification technique to achieve high undercooling. In present work, copper mould chilling was used for undercooled Fe-Co base alloy melts. On one hand, the latent heat of crystallization can be trans- mitted to outside more rapidly by copper mould, on the other hand, by increasing the cooling rate, copper mould can also make undercooled melt achieve further undercooling. In this work, applying fluxing purification and cycling superheating method, Fe44Co44Nb7B4Cu1 melts were undercooled, and microstructure evolutions of the two different kinds of Fe44Co44Nb7B4Cu1 alloy samples prepared by undercooling solidification and copper mould chilling were studied, respectively. Using SEM and EDS,