Abstract:The abnormal shutdown of the pressurized water reactor (PWR) nuclear power plants can be primarily attributed to the rupturing of the heat transfer tube of the steam generator. Regardless, stress corrosion cracking is the most important ageing mechanism associated with the primary water of the PWR. In this work, the damage behavior of alloy 690 was systematically investigated using high-temperature and high-pressure in situ scratching and electrochemical techniques to understand its corrosion behavior and failure mode and provide a reference for controlling the manufacturing, processing, and installation of the alloy 690 tubing. Further, the polarization behavior of alloy 690 at different temperatures was investigated using the self-built high-temperature and high-pressure water circulation circuit system and the high-temperature and high-pressure in situ scratching device. Subsequently, the single-pass scratch in air and in situ reciprocating scratch of alloy 690 obtained using high-temperature and high-pressure water for 11 and 100 h, respectively, were studied. The samples after scratching were observed and analyzed via SEM and EDS. The results revealed the occurrence of microcracks at the bottom of the scratch during the single-pass scratch of alloy 690. The TiN inclusions with large particles were prone to fragmentation, whereas those with smaller particles were susceptible to cracking at the joint of the matrix. During the reciprocating scratch process in high-temperature and high-pressure water, a portion of the metal substrate debris at the bottom of the scratch groove was peeled off along with oxide particles, microcracks, and chipped debris. Further, the TiN inclusions with large particles were fragmented, whereas those with smaller particles easily cracked at the bonding interface of the substrate. The electrochemical signals of alloy 690 during the reciprocating scratch processes were measured using the high-temperature and high-pressure in situ electrochemical technology. The instantaneous peak current density at the scratch during the scratch process is 149 similar to 326 times of that associated with the substrate.

Localized corrosion behavior of scratches on nickel-base Alloy 690TT

MICROSTRUCTURE NEAR SCRATCH ON ALLOY 690TT AND STRESS CORROSION INDUCED BY SCRATCHING

Effects of Scratching on Corrosion and Stress Corrosion Cracking of Alloy 690TT at 58°C and 330°C

Electrochemistry and in Situ Scratch Behavior of 690 Alloy in Simulated Nuclear Power High Temperature High Pressure Water

Effect of surface scratch depth on microstructure change and stress corrosion cracking behavior of alloy 690TT steam generator tube

Insights into stress corrosion cracking in scratched area of alloy 690TT steam generator tubes

Crevice Corrosion Behavior of Alloy 690 in High-Temperature Aerated Chloride Solution

Development of Prediction Model for Stress Corrosion Cracking Probability in Scratched Alloy 690TT Heat Transfer Tubes

High-resolution Characterization of the Fretting Corrosion of Alloy 690 in the Simulated Secondary Water of Pressurized Water Reactor

Stress Corrosion Behavior of Scratched Alloy 690TT Steam Generator Tube in Chlorine‐containing High‐temperature Pressurized Water

Microstructural Study on the Stress Corrosion Cracking of Alloy 690 in Simulated Pressurized Water Reactor Primary Environment

Corrosion Behaviour of Nanocrystallines Alloy 690 at High-Temperature and High-Pressure in Simulated PWR Secondary Environment

Microscopic Residual Stresses Beneath a Scratch and Their Effects on Scratch-Related Crack Initiation of Thermally Treated UNS N06690 in High-Temperature Pressurized Water

Corrosion Behavior of Alloy 690 in Aerated Supercritical Water

Fretting wear-induced sudden loss of corrosion resistance in a corrosion-resistant Ni-based alloy

Nodular corrosion inside the crevice of Alloy 690 in deaerated high-temperature chloride solution

The single effect of microstructure, residual strain and geometric structure on the stress corrosion cracking behavior of scratched alloy 690TT

Electrochemical study on the fretting corrosion synergistic damage mechanism of Inconel 690 alloy in different dissolved oxygen solution

Investigation on the Failure Mechanistic Evolution of Fretting Corrosion of Alloy 690 with Increasing Cycles in High-Temperature Water

CORROSION BEHAVIOR OF NUCLEAR GRADE ALLOYS 690 AND 800 IN SIMULATED HIGH TEMPERATURE AND HIGH PRESSURE PRIMARY WATER OF PRESSURIZED WATER REACTOR

Effects of Surface State and Applied Stress on Stress Corrosion Cracking of Alloy 690TT in Lead-containing Caustic Solution