Abstract:PANI/FeS2/MnO2 composite electrode materials were successfully prepared. The results showed that the specific capacitance of PANI/FeS2/MnO2 4 : 1 : 3 was 580 F/g at 1 A/g, and the capacitance retention rate was 85.2 % after cycling 10,000 times at 5 A/g. The asymmetric supercapacitor PANI/FeS2/MnO2 4 : 1 : 3 //AC had an energy density of 37.93 Wh/kg at a power density of 0.85 kW/kg. Polyaniline (PANI) has unique physical and chemical peculiarities, so it has been widely researched in the field of energy storage. However, its structure is easy to be damaged during charging and discharging, which seriously affects its application. PANI/FeS2/MnO2 composite materials were successfully prepared by an easy combination of chemical precipitation and chemical oxidative polymerization. The electrochemical test results manifested that the specific capacitance of PANI/FeS2/MnO2 4 : 1 : 3 was 580 F/g at 1 A/g, and had great cyclic stability (capacitance retention rate was 85.2 % after 10000 cycles at 5 A/g). It was because that reticular structure shortened the ion transport path. On the other hand, it was able to effectively mitigate the volume change during long‐term charging and discharging, thus improving the cycling stability. In addition, PANI/FeS2/MnO2 4 : 1 : 3 as the positive and activated carbon (AC) as the negative, an asymmetrical supercapacitor was assembled with a maximal energy density of 37.93 Wh/kg when its power density was 0.85 kW/kg. At the same time, the device possessed a long cycle life (the capacitance conservation rate was 82 % after 5000 cycles at 5 A/g). This excellent performance is due to the excellent synergy between the PANI, FeS2 and MnO2. This study opens a new way to investigate polyaniline‐based composite electrode materials.

ELECTROCHEMICAL SYNTHESIS OF COMPOSITE MATERIALS AND PERFORMANCE STUDY

Synthesis of γ-MnO 2 /PANI Composites for Supercapacitor Application in Acidic Electrolyte

A Coralliform-Structured Γ-Mno 2 /polyaniline Nanocomposite for High-Performance Supercapacitors

Fabrication of Nanocomposite Electrode with MnO2 Nanoparticles Distributed in Polyaniline for Electrochemical Capacitors

Synthesis and Electrochemical Characteristics of Polyaniline-MnO2 Nanocomposites

Synthesis and Supercapacitance Performance of PANI/MCFs Materials

MnO 2 /polyaniline Hybrid Nanostructures on Carbon Cloth for Supercapacitor Electrodes

MnO2/polyaniline hybrid nanostructures on carbon cloth for supercapacitor electrodes

Fabrication of Polyaniline/mesoporous Carbon/mno2 Ternary Nanocomposites and Their Enhanced Electrochemical Performance for Supercapacitors

Synthesis and electrochemical testing of polyaniline attached manganese dioxide and functionalized multi-walled carbon nanotubes based active composite material

Supercapacitor Performance of in Situ Polymerization for PANI/MnO2-TiO2

Simultaneous Preparation of Polyaniline Nanofibers/Manganese Dioxide Composites at the Interface of Oil/Water for Supercapacitive Application

Development of PANI/FeS2/MnO2 Composite Electrode Materials for High‐Performance Supercapacitors

Synthesis of NiMn2O4/PANI Nanosized Composite with Increased Specific Capacitance for Energy Storage Application

Electrical and electrochemical studies of core–shell structured nanorods of LiMn2O4@PANI composite

Electrodeposition of PANI/MnO2 Composite on SnO2/Ti Substrate for Supercapacitor Electrode

Facile Synthesis of a Ni-based NiCo2O4-PANI Composite for Ultrahigh Specific Capacitance

Electrochemical Synthesis of Layer-by-layer Reduced Graphene Oxide Sheets/polyaniline Nanofibers Composite and Its Electrochemical Performance

Construction of Mesoporous Carbon Microsphere/polyaniline Composites As High Performance Pseudocapacitive Electrodes

Synthesis and high electrochemical performance of polyaniline/MnO2-coated multi-walled carbon nanotube-based hybrid electrodes

Electrochemical Deposition of PANI/PEDOT:PSS Composite Polymer for Supercapacitors Application