Incorporating three-dimensional ordered macropores into high-entropy oxides for catalytic soot combustion
Xiaolan Duan,Xiaopeng Wang,Lan Xu,Tingting Ma,Yuan Shu,Shengtai Hou,Qiang Niu,Pengfei Zhang
DOI: https://doi.org/10.1039/d3ta00827d
IF: 11.9
2023-09-04
Journal of Materials Chemistry A
Abstract:Since 2018, high entropy oxides (HEOs) have been introduced to the catalysis community, due to their tunable compositions, abundant lattice distortion, and excellent thermal stability. Although porous structure is usually essential for heterogeneous catalysts, the synthesis of porous HEOs using both traditional hard and soft templates failed. Herein, inspired by the self-assembly behavior of polystyrene (PS), various HEOs with three-dimensional ordered macro-porous (3DOM) structure, including cubic Ce 0.5 Ni 0.1 Mg 0.1 Cu 0.1 Zn 0.1 Co 0.1 O x , cubic Zr 0.5 Ni 0.1 Fe 0.1 Cu 0.1 Mn 0.1 Co 0.1 O x , spinel Ni 0.2 Mg 0.2 Cu 0.2 Mn 0.2 Co 0.2 Al 2 O x , and perovskite LaNi 0.2 Fe 0.2 Co 0.2 Cr 0.2 Mn 0.2 O x , were prepared. Together, the uniform distribution of metal precursors inside the PS matrix and the decreased crystallization temperature due to the increased configuration entropy facilitated the formation of 3DOM-HEOs. The crystallization process was monitored by in situ X-ray diffraction. Interestingly, Ce 0.5 Ni 0.1 Mg 0.1 Cu 0.1 Zn 0.1 Co 0.1 O x with ordered macropores, active oxygen species, and high entropy-stabilized structure exhibits competitive activity ( T 50 = 393 °C) in soot combustion under harsh conditions (4.2 vol% moisture, 20 ppm SO 2 ), higher than those of the sol–gel control sample ( T 50 = 419 °C), 3DOM-CeO 2 ( T 50 = 506 °C), commercial CeO 2 ( T 50 = 519 °C) and 1% Pt/Al 2 O 3 ( T 50 = 595 °C).
materials science, multidisciplinary,chemistry, physical,energy & fuels