Microstructure and Properties of TC4 Alloy With Electrical Discharge Surface Strengthening

Li Min,Wang Hongwei,Cai Lanrong,Liu Pengxin

DOI: https://doi.org/10.3969/j.issn.1007-2330.2013.03.019

2013-01-01

Abstract:The electric spark deposition method was used to strengthen TC4 alloy surfaces(with or without carbide layer coating,respectively) under kerosene-based oil or misted deionized water medium conditions.The microstructure,phase compositions and microhardness of strengthened layer were investigated.The results indicated that microstructure of strengthened layer showed chrysanthemum petal-like.Under kerosene-based oil medium condition,compared with uncoated surfaces the quantity of carbide after coating on alloy surface was increased,which were overlapping on edges of petals as while.Under misted deionized water medium condition,the distribution of carbides on strengthened layer was more disperse and uniform.Analysis for phase composition of strengthened layer showed that it was composed of α-Ti and TiC.In addition,compared with primary TC4 alloy,the microhardness of strengthened layer was improved significantly.The microhardness was measured to be about 800 MPa under both medium condition while it showed more stable performance in misted deionized water medium condition.