Fabrication and Oxidation Behavior of a Reaction Derived Graphite–zrc Composite for Ultrahigh Temperature Applications

Wenbo Han,Zhi Wang

DOI: https://doi.org/10.1016/j.matlet.2009.07.022

IF: 3

2009-01-01

Materials Letters

Abstract:Graphite containing nominally 40 vol.% ZrC (graphite-ZrC) was prepared from commercially available ZrO2 and graphite powders by hot pressing at 2000 degrees C in a vacuum. The oxidation behavior of the graphite-ZrC composite was carried out in dry stagnant air at the temperatures of 1200 and 2200 degrees C. Compared with the pure graphite, the graphite-ZrC composite exhibited good oxidation resistance because the mass loss of the composite powder was significantly lower than that of the pure graphite. The mass loss of graphite-ZrC at 2200 degrees C was lower than pure graphite at 1200 degrees C. Furthermore, the introduction of ZrC also improved the strength of the graphite-ZrC composite. (C) 2009 Elsevier B.V. All rights reserved.